4.4 Report of project part 04: Epitaxial lead salt nanostructures
Epitaxial lead salt nanostructures for mid-infrared lasers and detectors
Principal investigator: Gunther Springholz
Institut für Halbleiter- und Festkörperphysik
Johannes Kepler Univeristät
Altenbergerstr. 69, A-4040 Linz
Phone: +43 (0)732 2468 9602
Fax: +43 (0)732 2468 8650
eMail: [email protected]
Report – Project description
4.4.1 Summary
The realization of self-assembled quantum dots with efficient emission in the mid-infrared
spectral region has remained a considerable challenge. In this project, therefore, novel self-
assembled semiconductor quantum dots were fabricated based on the lead salt compounds.
Due to their narrow band gaps and favourable electronic band structure as well as the low
non-radiative Auger recombination rates, these compounds are very well suited for mid-infra-
red devices. Self-assembled quantum dots were fabricated by strained-layer heteroepitaxy
using the Stranski-Krastanow growth mode as well as a novel alternative method based on
phase separation and nanoprecipitation. To obtain quantum dots with high emission efficien-
cy, strain-tuning and band gap engineering was applied. Detailed growth investigations were
performed for the PbSeTe quantum dot system for a wide range of compositions and strain
values ranging from 0 to 5.4%. By changing the buffer layer, tensile as well as compressively
strained dots were produced and their structural and electronic properties investigated in
detail with respect to their applicability for mid-infrared optoelectronic devices. Based on in
situ scanning tunneling microscopy, a strong intermixing between the dots and the matrix
material was found. This effect could be suppressed by alloying of the capping material. As
derived from optical spectroscopy investigations, PbSe dots exhibit a type II band alignment
to the surrounding barrier material due to the strong strain effects on the electronic band
structure. This arises from the large deformation potentials which were determined
experimentally from optical spectroscopy of strained-layer structures. As a consequence,
mid-infrared optical emission of these dots is too weak for obtaining stimulated emission.
To solve this problem, we have developed a new class of self-assembled quantum dots
based on the combination of zinc blende II-VI and rock salt lead salt compounds. Due to the
wide miscibility gap, phase separation and nanoprecipitation of highly symmetric PbTe
quantum dots in CdTe with extraordinary structural and optical properties occurs. Due to their
defect free and atomically sharp heterointerfaces as well as the excellent carrier confinement
arising from the large 1.5 eV difference of the PbTe/CdTe band gaps, intense room tempe-
rature photoluminescence emission in the range of 2 – 3.5 µm wavelength was obtained.
With respect to mid-infrared devices, we have developed improved Bragg mirrors and micro-
cavity structures, which were applied for fabrication of vertical cavity surface emitting lasers
and narrow band width mid-infrared detectors integrated interference filters were produced.
The project work involved successful collaborations with several other SFB partners, in
particular with P2 for transmission electron microscopy, P7 for x-ray diffraction, P5 and P12
for optical spectroscopy and P6 for ab initio calculations. This is documented by a large
number of common publications in scientific journals as well as presentations at conferences.
P04 Epitaxial lead salt nanostructures (Springholz)
4.4.2 Scientific Background – State-of-the-Art
Self-assembled semiconductor quantum dots fabricated directly by epitaxial growth have
attracted tremendous interest due to their novel physical properties as well as their great
potential for device applications. In most the most common scheme, these quantum dots are
synthesized by the Stranski-Krastanow growth mode of strained-layer material systems
(Leonhard1993) in which nanometer sized 3D islands spontaneously nucleate on the surface
of a thin 2D wetting layer. This results from the fundamental surface instability of strained
layers that is driven by the large reduction of strain within the islands due to lateral elastic
expansion or compression in the direction of the free side faces (Shchukin2003). The most
promising applications of self-assembled quantum dots are in the field of optoelectronics due
to the sharply peaked electronic density of states. Theoretically, quantum dot lasers have
been predicted to yield strongly increased material and differential gain (Asada1986), lower
threshold currents, higher modulation band widths and better temperature stability (Arakawa
1982). As demonstrated by recent work, indeed self-assembled InAs/GaAs quantum dot
lasers (Kirstaedter1994) outperform conventional quantum well lasers and ultra-low threshold
currents have been achieved (Huang2000). Up to now, however, quantum dot lasers have
been made exclusively from III-V semiconductors with emission wavelengths in the visible or
near infrared spectral regions (Grundmann2002).
The realization of self-assembled quantum dots with efficient mid-infrared emission at wave-
lengths beyond 2 µm has remained a considerable challenge. This is because for Stranski-
Krastanow quantum dots the high epitaxial strains imposed by the surrounding barrier
material drastically change the energy gaps and band alignments due to the deformation
potentials (Stier1998, Williamson1999, Pryor2005, Simma2006). As a result, the effective
band gaps of III-V semiconductor quantum dots are strongly increased and thus, even
narrow gap InAs or GaSb quantum dots emit in the near-infrared rather than the mid-infrared
spectral region (Leonhard1993, Moison1994, Glaser1996, Moltan2002). For the classical
InAs quantum dots, e.g., the compressive strain induced by the 7 % lattice mismatch to the
GaAs matrix doubles the 0.41 eV InAs band gap to more than 0.8 eV (Stier 1998,
Williamson1999), and with the additional quantum confinement shift, the dots typically emit at
wavelengths between 0.9 – 1.4 µm (Leonhard1993, Moison1994, Grundmann2002). For
antimonide GaSb or InSb quantum dots, the situation is complicated due to the staggered
type II band alignment to most III-V barrier materials (Van de Walle1989, Vurgaftman 2001).
As a result only one type of carrier is confined within the dots and due to the corresponding
spatially indirect optical transitions the luminescence emission is rather weak in these cases.
As revealed by a recent survey of band alignments in III-V nanostructures (Pyror 2005), a
type I band alignment for efficient mid-infrared emission is difficult to achieve with III-V
Report – Project description
quantum dot materials and only very recently, InSb/GaSb quantum dots with infrared
emission beyond 2 µm have been obtained (Tasco2006). Therefore, up to now III-V quantum
dot lasers have been obtained only for visible or NIR emission (Grundmann2002).
The narrow band gap IV-VI semiconductors or lead salt compounds represent an attracttive
alternative class of materials for mid-infrared devices. This is due to the favourable electronic
properties of the lead salt compounds (Bauer2005) such as the mirror-like electronic band
structure with direct and narrow energy band gaps and the one order of magnitude lower
non-radiative Auger recombination rates (Findlay1998) as compared to narrow gap III-V or II-
VI compounds. As a consequence, lead salt diode lasers (Feit1996, Katzir1998,
Schiessel1999), covering a wide spectral region from 2 - 30 µm (Tacke1995, Katzier1989).
Due to their ultra-narrow line widths and their inherent wavelength tunability, lead salt lasers
have been used successfully in many high resolution spectroscopy applications (Tacke1995,
Katzir1989) such as molecular trace gas analysis (DeBacker1998), monitoring of gaseous
pollutants (Grisar1992), medical diagnostics (Sandstrom1999, Stepanov 2002) and time-
resolved analysis of industrial combustion processes. Apart from conventional edge emitters,
the development of lead-salt based ultra-high reflectivity Bragg mirrors (Schwarzl1999,
Springholz2006) has allowed the fabrication of the first mid-infrared vertical cavity surface
emitting lasers (VCSELs) by our group (Schwarzl1999) for which above room temperature
operation has been recently achieved (Heiss2001, Springholz2006, Schwarzl2007). On the
detector side, IV-VI infrared detector arrays have been successfully fabricated directly onto
silicon substrates with preprocessed integrated read-out electronics (Alchalabi2001], repre-
senting a new approach for monolithic integration of infrared photo detectors.
With respect to lead salt nanostructures, the fabrication of self-assembled quantum dots was
first demonstrated by our group in Linz for the PbSe/PbEuTe material system (Pinczolits
1998). Detailed investigations revealed various aspects of growth such as facetation
(Pinczolits 1999), control of dot sizes and densities (Raab2002), thermal stability (Raab2000)
and ordering in superlattice structures (Springholz 1998, 2000). An important highlight was
the discovery of a novel self-organized fcc-like ABC… dot stacking in PbSe quantum dot
superlattices that gives rise to an extremely efficient lateral ordering process. As a result,
nearly perfect 3D quantum dot crystals with tunable lattice constants were made (Springholz
1998). This was explained by a theoretical model that allowed the prediction of different kinds
interlayer correlations for other material systems (Holy1999) as well as their dependence on
dot size and layer thicknesses (Springholz2000). Other groups have demonstrated the
fabrication of uniform PbSe quantum dots onto Si (111) substrates with predeposited lead
salt buffer layers (Alchalabi2003)], and IV-VI quantum dots were also synthesized on BaF2
(Ferreira2001) and InP substrates (Probrajenski2000). Also, self-assembled PbSe quantum
P04 Epitaxial lead salt nanostructures (Springholz)
dots have been utilized for the fabrication of highly efficient thermoelectric devices as shown
by in a recent Science paper (Harman2002).
Up to the start of the project, most studies on self-assembled lead salt quantum dots had
focused on Stranski-Krastanow PbSe dots. Moreover, only their growth and structural
properties had been investigated and only little was known about the electronic and optical
properties of these dots which were found to yield only rather weak photoluminescence
emission. The objective of the project was therefore to study the electronic properties of the
dots in detail to clarify the nature of the optical transitions and complement these studies by
the investigation of the shape and composition of the buried dots embedded in various matrix
materials. In addition, strain engineering as well as the combination of new material systems
were planned to be investigated in order to increase the emission efficiency. With the
optimized dots emitter as well as photon detectors were to be realized. The investigations
thus encompassed a wide range of activities ranging from detailed growth studies, materials
development, structure characterization, optical spectroscopy as well as device fabrication.
4.4.3 Results and Discussion
As stated in the original application, the goal of this research project was to “develop novel
lead salt nanostructures for fabrication of mid-infrared quantum dot lasers and detectors”.
The latter requires quantum dot structures with strong carrier confinement and excellent
luminescence properties. The work packages of this project covered (i) the development of a
new material basis for mid-infrared active quantum dots and the investigation of their growth
properties, (ii) the determination of their structural and optical properties, (iii) the
development of ultra-high reflectivity Bragg mirrors and microcavity devices as well as the
realization of mid-infrared lasers and detectors. Several new material combinations were
investigated for fabrication of lead salt quantum dots such as strain-tuned ternary PbSeTe
quantum dots under compressive as well as tensile strain, and we have introduced Sr-based
instead of the Eu-based alloys as barrier material. As a completely new material system, the
growth of PbTe/CdTe quantum dots with very large quantum confinement and exceedingly
high luminescence efficiency was demonstrated. The results were published more than 20
papers in peer-reviewed scientific journals, among them one in Physical Review Letters and
six in Applied Physics Letters. The majority of the papers resulted from joint research work
with one or more SFB partners, which demonstrates the strength of the collaborations
developed in the IR-ON partnership. In the following, the most important results of the project
areas are summarized.
Report – Project description
Shape transitions of buried PbSe quantum dots
Overgrowth of quantum dots leads to significant changes in shape and composition due to
intermixing with the surrounding capping material. In this project, a novel technique for inves-
tigation of the buried dot structure was developed based on scanning tunneling microscopy
measurements and analysis of the surface displacements induced by the buried dots as
shown in Fig. 1 (Abtin2006, Springholz2007). This was applied for PbSe dots as a model
system, focusing on the role of the chemical composition of the capping material on the over-
growth process. In particular, the surface evolution was found to differ drastically between
capping with PbTe or PbEuTe layers. For the former, the pristine PbSe pyramids rapidly
shrink and transform into flat and rounded dots, whereas for the latter the dot shape is com-
pletely preserved. This was explained by difference in bond energy between PbTe and EuTe,
where the presence of EuTe suppresses the intermixing between dots and matrix material.
The same was also found when SrTe is introduced into the capping material (Abtin2008).
-40 -30 -20 -10 0 10 20 30
-3.0
-2.5
-2.0
-1.5
-1.0
-0.5
0.0
-40 -30 -20 -10 0 10 20 30 40
-2.5
-2.0
-1.5
-1.0
-0.5
0.0
0.5
d = 60 ÅxSe = 55%
d = 40 Å
Dep
th (Å
)
(a) Varying base width
60°
(d) Varying composition(c) Varying facet angle
xSe = 55%
240Å 280Å 320Å 360Å 400Å 440Å 480Å520Å
(b) Varying base widthd = 60 Å
Lateral direction (nm)
STM
d = 60 Åb = 340Å
15°
xSe=
STM
STM STM
30%
30°20°
10°
100% 90% 80% 70% 60% 50% 40%
b = 240Å 280Å 320Å 360Å 400Å 440Å 480Å520ÅxSe = 55%
Dep
th (Å
)
Figure 1: Left: STM images of PbSe dots covered with PbTe cap thicknesses of 30, 40, 80 and 120 Å from (a) to (d), respectively. The inserts show the facetted pyramidal shape of the uncapped dots (a) and the zoomed-in image of a single surface depression induced by a buried dot (b). Right: Calculated surface depression profiles for different dot shapes (gray lines) for different dot parameters as indicated in the figures plotted in comparison with the STM profiles (blue lines). d is the cap thickness, xSe the Se concentration, α the side wall angle, and b the dot base width. Best agreement was found for xSe = 55%, b = 340 Å, α = 20° and a dot height of 30Å (Springholz2007).
For quantitative determination of the dot structure, we have developed a structure model
combined with elasticity calculations. By this novel approach the shape and chemical compo-
sition of the buried dots was deduced. The influence of the capping process on the dots was
independently investigated by synchrotron x-ray scattering experiments performed at the
ESRF in Grenoble (Holy2005, Schülli2004). The obtained results are in good agreement with
the STM measurements. We have also performed a series of studies on surface exchange
P04 Epitaxial lead salt nanostructures (Springholz)
reactions in mixed anion IV-VI heterostructures, demonstrating an almost complete Se for Te
surface exchange under chalcogen-rich MBE conditions. Moreover, we showed that this
effect can be also utilized for synthesis of self-assembled PbSe quantum dots.
Self-assembled PbTe quantum dots
The growth of compressively PbTe quantum dot on PbSe (111) was studied for the first time.
The critical thickness for dot formation was found to be 1.5 monolayers and it significantly
decreases with decreasing temperature. With increasing PbTe thickness and in-creasing dot
size, a shape transformation of the dots from {100} facetted pyramids to truncated pyramids
and finally truncated hexagons was found as shown in detail by Fig. 2. Correspondingly, the
aspect ratio of the dots decreases. For a given growth temperature, the PbTe dot size is
much larger and the density much lower compared to those of PbSe dots. While this could
be expected from the much larger surface diffusion lengths of PbTe growth due lower binding
energy, the Arrhenius analysis of the density as a function of temperature shows that the
activation energy for dot formation are quite similar in both systems but only the pre-
exponential factor is drastically reduced for PbTe dots. Due to the larger dot size, a very slow
surface planarization occurs during overgrowth of PbTe dots. Therefore, for multilayer dot
structures much larger spacer thicknesses are required and therefore, no interlayer corre-
lations are formed in great contrast to PbSe quantum dot superlattices.
Figure 2: AFM images of PbTe dots on PbSe (111) at coverages of 1, 2, 3 and 8 monolayers from (a) to (d). (e) PbTe dot height h versus dot width w evaluated for four different PbTe coverages from 2 to 8 monolayers. The shape evolution of the dots is shown schematically in (f) and consists of three stages, namely, (i) small dots with pyramidal shape defined by {100} side facets (ii) intermediate dots with truncated pyramidal shape and lower aspect ratio, and (iii) large dots with truncated hexagonal shape arising from the additional {110} side facets.
Report – Project description
Self-organized ordering and stacking quantum dot superlattices
Stacking of quantum dot layers in multilayer structures was investigated a method for
improving the ordering and uniformity of the dots. In particular, we have performed studies on
the lateral ordering process of PbSe and ternary PbSeTe quantum dots separated by
PbEuTe and PbSrTe spacers (Lechner2004) and have shown that the ordering is strongly
influenced by the chemical composition of the spacer layers. This was explained by the
strong intermixing between the dots and matrix material, which modifies the surface strain
distributions responsible for interlayer correlations. The ordering process was also modeled
by Monte Carlo growth simulations, by which the transitions between different dot stacking
types as a function of thickness and composition of the spacer layers could be quantitatively
explained (Springholz2006, 2008).
Strain tuned PbSeTe quantum dots
Strain is a crucial prerequisite for formation of Stranski-Krastanow quantum dots but also
strongly influences their electronic properties due to strain-induced changes in the band
structure. Therefore, we have investigated in detail the dependence of the growth and optical
properties of dots as a function of strain by using ternary PbSeTe alloys with varying
composition as dot material and PbTe or PbSe buffer layer as pseudo-substrates.
Figure 3: Comparison of AFM images of tensile (top) and compressively (bottom) PbSeTe dots grown on PbTe, respectively PbSe buffer layers. In both cases the coverage was 3, 5, and 7 monolayers for composition of x = 100, 60 and 50 %, from (a) to (c), and (d) to (f), respectively. Note the different scale of the AFM images: Top 1x1 µm2, bottom 3x3 µm2.
P04 Epitaxial lead salt nanostructures (Springholz)
This results in tensile, respectively, compressively strain dots and the magnitude and sign of
strain can be varied over the whole range from 0 to ± 5.4%. From systematic growth studies
(see AFM images of Fig. 3), the complete growth phase diagrams were established in both
cases as a function of composition and layer thickness as shown in Fig. 4. In particular, the
critical wetting layer thickness for dot formation was shown to increases rapidly with
decreasing misfit strain and a transition from 3D island growth to 2D layer-by-layer growth
was found at a critical strain value of about 2 %. At lower values, the strain is relaxed
exclusively by misfit dislocations. For the different material composition and sign of strain, the
evolution of dot sizes, shapes and size distributions was also determined quantitatively by
atomic force microscopy measurements.
Tensile strained PbSeTe on PbTe (111) Compressive PbSeTe on PbTe (111)
0.0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 1.1
10
100
1000
0
AFM-2D AFM-Transiton AFM-3D RHEED Θc2 RHEED Θc1 AFM 2D-MD :Transition hMDMatthews-Blakeslee
2D+MDPb
TexS
e 1-x th
ickn
ess
(ML)
Tellurium concentration xTe
2D
0.0 0.1 0.2 0.3 0.4 0.5 0.6 0.7 0.8 0.9 1.01
10
100
1000
Figure 4: Phase diagram of critical thickness versus layer composition for growth of (a) tensile strained PbSexTe1-x quantum dots on PbTe buffer and (b) compressively strained PbTexSe1-x dots on PbSe buffer layers. Open symbols indicate the layer thickness where 2D growth is observed, full symbols the layer thicknesses where 3D dots are found by AFM. Full circles indicate the critical thickness observed by in situ RHEED.
PbTe/CdTe quantum dots
To overcome the weak carrier confinement in strained PbSeTe SK quantum dots, we have
fabricated quantum dots from the PbTe/CdTe material system. This combines materials with
large difference in band gap and crystal structure (rock salt versus zinc blende type), but with
nearly matched lattice constant. As revealed by our detailed growth and electron microscopy
studies, due to the absence of strain quantum dot formation relies on a completely different
mechanism that for the usual SK dots. In buried PbTe/CdTe heterostructures, thin 2D PbTe
layers transform into isolated octo-cubo-octahedral quantum dots after thermal treatment.
This transformation results from the immiscibility of the material system and is driven by the
lowering of the inter-face energy by phase transition. As a result, these nanoprecipitate
quantum dot exhibit completely different properties compared to the usual SK dots, namely,
the formation of highly symmetrical shapes and atomically sharp interfaces without any signs
2D+MD
Selenium concentration xSe
2D3D
AFM-2D AFM-Transiton AFM-3D RHEED Θc2 RHEED Θc1 AFM 2D-MD :Transition hMDMatthews-Blakeslee
PbSe
xTe 1
-x th
ickn
ess
(ML)
2D+MD2D+MD
3D 3D
Report – Project description
of alloy intermixing. Moreover, the emission of such PbTe/CdTe quantum dots is extremely
bright and can be tuned over a wide wavelength region from about 3.5 to 2 µm by changing
the size of the dots. This can be accomplished by control of the initial PbTe layer thickness
as well as by the post growth annealing conditions.
(c)
(b)
(a)
inte
nsity
(arb
. uni
ts)
Figure 5: (a) Cross sectional TEM image of a PbTe/CdTe multilayer sample containing four PbTe layers with 1, 2, 5 and 10 nm thicknesses subjected to 10 min post-growth annealing at 360°C to transform the PbTe layers into isolated quantum dots. (b) Dot height histograms for the 1, 2 and 5 nm layers, indicating a substantial increase of dot size with increasing PbTe layer thickness. (c) Room temperature photoluminescence spectra of PbTe/CdTe quantum dots for the multilayer as well as single layers with 1, 3 and 10 nm thicknesses (Groiss 2007).
Infrared spectroscopy and band offsets of PbSeTe quantum dots
From photo-luminescence investigations of highly strained PbSe quantum dots the emission
was found to be rather weak compared to unstrained quantum wells. To resolve this issue,
photoconductivity experiments on PbSe/PbEuTe quantum dot multilayers were performed as
shown in Fig. 6. We found a significant blue shift of the photoconductivity onset with
decreasing dot size, but the absence of a photocurrent freeze out at low temperatures
indicates a type II band offset between the dots and the matrix material. According to our
model calculations (see Fig. 6(d)), this is due to the strong downward shift of the PbSe
valence band edges by the tensile dot strain, which means that photo-excited holes are not
confined in the dots. For quantitative determination of the band offsets and deformation
potentials of PbSe, we have fabricated series of PbSe/PbEuSeTe multi quantum well
structures in which the strain in the PbSe wells was varied over a wide range. From FTIR
spectroscopy studies, we found a type I – type II transition at a strain value of ~1% and from
the shifts of the energy levels as a function of strain, the deformation potentials were
deduced. While this configuration yields an excellent photo response signal for detector
applications, for high luminescence emission a type I band alignment is required. Therefore,
we have investigated ternary quantum dots with reduced strain values and increased barrier
P04 Epitaxial lead salt nanostructures (Springholz)
height. Although a significant improvement in luminescence efficiency was obtained in this
way, the limitation due to insufficient hole confinement could not be resolved.
unstrained case
strained case
(a)
(b)
(c)
(d)
Figure 6: Lateral photocurrent measurements (solid line) at PbSe QDs with different dot size (dotted line: simulation of PC signal). The arrows mark the transition energies in the different structures of the QD superlattice. E1
s/p (E2s/p) transition to dot ground (first excited) s/p-states, E1
l/o transition to longitu-dinal and oblique wetting layer ground states, Eg,b barrier band gap. Insets: AFM images of the QDs (Simma2006).
Devices
High reflectivity Bragg mirrors constitute one of the crucial elements of high finesse micro-
cavities and vertical cavity emitting lasers (VCSELs). For the infrared spectral region,
dielectric layers with large refractive index contrast are needed in order to keep the total
thickness of epitaxial Bragg mirrors at a value feasible for MBE growth. In this project we
have developed new types of Bragg mirrors based on the ternary PbSeTe/EuSe/BaF2
material system which can be lattice matched for a certain PbSeTe ternary composition and
which features a very high refractive index contrast of up to 100% (Springholz2005). The
Bragg mirrors and microcavity structures were characterized by AFM, x-ray diffraction and
FTIR spectroscopy and samples were provided to P5-Heiss for fabrication of nanocrystal
devices. Due to the high refractive index contrast, these mirrors exhibit unique properties like
omni-directionality (Baumgartner2006) and tunability of the sharp cavity resonance by
changing of the incidence angle as shown by Fig. 7(a) and (b). With these novel Bragg
mirrors, vertical cavity surface emitting lasers with record performance values were produced
with cw emission at wavelengths between 5.9 and 8 µm and operation temperatures up to
140K, as shown by the emission spectra displayed in Fig. 7(d) and (e). Currently, we aim at
Report – Project description
further increasing the operation temperatures and to incorporate PbTe/CdTe quantum dots
into the active region of the VCSEL structure.
(c) (d)
(e)
Figure 7: (a) Transmittance spectra of a high-finesse BaF2/PbEuTe microcavity structure plotted as a function of incidence angle, showing the broad stop band region with the central sharp cavity reso-nance peak. The λ/2 cavity was fabricated from high-reflectivity BaF2/PbEuTe Bragg mirrors grown by MBE. (b) Plot of the stop band edges and cavity resonance as a function of incidence angle for TM and TE polarizations obtained from experiments (open symbols = TE, filled = TM) compared to model calculations (solid/dashed lines) (Baumgartner2006). (c) and (d) MIR cw laser emission recorded for a VCSEL made from such mirrors at 54 and 135 K with the layer structure indicated by the cross-sectional electron microscopy image shown in (e) (Schwarzl2007).
Apart from the VCSELs we have also started to produce PbTe/CdTe micropillar lasers, but
up to now only strong spontaneous but no stimulated emission was obtained due to the not
optimized etching conditions, resulting in a too high side wall roughness of the micropillars.
For the infrared detectors, the photo response of type II PbSe/PbEuTe quantum dots was
characterized in detail in collaboration with partner P12 (Simma2006), indicating a high photo
conductive gain even at room temperature. Antireflection coatings were developed in order to
minimize the multiple interference fringes arising from the substrate reflection. Adding an
epitaxial narrow band interference filter structure allowed to fabricate mid infrared detectors
with a narrow spectral response (Böberl 2006) that was tuned exactly to the O-C-H stretching
vibration as required, e.g., for the optical detection of acetaldehyde.
4.4.4 Collaboration within and beyond the SFB
To achieve the wide range of innovative results, intense collaborations have been estab-
lished within this SFB program as well as several groups outside of Austria. These collabora-
tions involved the exchange of samples, sharing of measurement results, experimental set-
ups and instrumentation, exchange of expertise and know-how, common publications as well
P04 Epitaxial lead salt nanostructures (Springholz)
as joint supervision of diploma and PhD students. Specifically, the project was supported by
partners P2-Schäffler, P5-Heiss, P7-Stangl and P12-Fromherz with material analysis and
characterization using transmission electron microscopy, x-ray diffraction, optical spectros-
copy, modeling as well as design and processing of devices. Samples were provided to P2
for detailed TEM investigations as well as to P5 for further device fabrication. Know-how
concerning laser fabrication was obtained from partner P3-Strasser. Theoretical input was
received from partners P6-Bechstedt/Kresse by ab initio calculations of the electronic band
structure of the lead salt compounds as well as of the interface structure of PbTe/CdTe dots.
The latter strongly contributed to the development of an improved understanding of the novel
quantum dot system. Our group provided partners P2, P5, P7 and P12 with AFM expertise
and instrumentation for characterization of self-assembled quantum dots, nanocrystals as
well as patterned nanostructures. Evidently, the strong links and intense collaborations within
the IR-ON research program have generated tremendous synergies and have thus resulted
in a large number of common publications.
P4-Springholz
P2-TEM investigations
P6-ab initio calcuations
P5-spectroscopy & microcavities P12-detectors
spectroscopy P7-X-ray
diffraction
Figure 8: Integration of the project P4 within the SFB. Joint research work was performed with partners P2-Schäffler, P5-Heiss, P6-Kresse/ Bechstedt, P7-Stangl, and P12-Fromherz. This involved exchange of samples, sharing of measurement results, use of instrumentation, exchange of expertise and ideas, and common publications and joint supervision of diploma & PhD students.
Concerning the collaboration with external groups, the modeling and analysis of the structure
properties and growth of self-assembled quantum dots was strongly supported by the group
of Prof. Vaclav Holy at the University of Prague, mid-infrared laser spectroscopy measure-
ments were performed in the group of Prof. Harald Pascher, the group of Dr. T. Wojtowicz at
the Institute of Physics at the Polish Academy of Sciences in Warzawa has supplied us with
very high quality virtual substrates for II-VI / IV-VI heteroepitaxy and with the group of Prof.
Yano at the Osaka Institute of Technology we have developed the novel method for
synthesis of PbTe/CdTe quantum dots by the nanoprecipitation process.
Report – Project description
4.4.5 References
Abtin L., G. Springholz, and V. Holy (2006), Surface Exchange and Shape Transitions of PbSe Quantum Dots during Overgrowth, Phys. Rev. Lett. 97, 266103-6.
Abtin L. and G. Springholz (2008), Stabilization of PbSe quantum dots by ultra-thin EuTe and SrTe barrier layers, submitted to Appl. Phys. Lett.
Alchalabi K., D. Zimin, G. Kostorz, H. Zogg (2003), Self-Assembled Semiconductor Quantum Dots with Nearly Uniform Sizes, Phys. Rev. Lett. 90, 026104.
Alchalabi, K. Zimin, D. Zogg, H. Buttler, W. (2001), Monolithic heteroepitaxial PbTe-on-Si infrared focal plane array with 96×128 pixels, IEEE Electron. Device Lett. 22, 110.
André R. and Le Si Dang (1997), Low-temperature refractive indices of Cd1-xMnxTe and Cd1-yMgyTe , J. Appl. Phys. 82, 5086.
Arakawa Y., and H. Sakaki (1982), Multidimensional quantum well laser and temperature dependence of its threshold current, Appl. Phys. Lett. 40, 939.
Asada M., Y. Miyamoto, Y. Suematsu (1986), Gain and the threshold of three-dimensional quantum-box lasers, IEEE J. Quantum Electron. 22, 1915.
Bauer G. and G. Springholz (2005), Fundamental Properties of Lead Salts, in: Encyclopedia of Modern Optics, ed. B. D. Guenther (Elshevier) p. 385-392.
Baumgartner, E., T. Schwarzl, G. Springholz, W. Heiss (2006), Highly efficient epitaxial Bragg mirrors with broad omnidirectional reflectivity stop bands in the mid-infrared, Appl. Phys. Lett. 89, 051110.
Böberl, M., T. Fromherz, J. Roither, G. Pillwein, G. Springholz, W. Heiss (2006), Room temperature operation of epitaxial lead-telluride detectors monolithically integrated on mid-infrared filters, Appl. Phys. Lett. 88, 041105
De Backer Barilly M. R., B. Parvitte, X. Thomas, V. Zeninari, D. Courtois (1998), Tunable diode laser spectrometer apparatus function, J. Quant. Spectros. Radiative Transfer 59, 345.
Deguffroy N., V. Tasco, A. N. Baranov, E. Tournié, B. Satpati, A. Trampert, M. S. Dunaevskii, A. Titkov, and M. Ramonda (2007), Molecular-beam epitaxy of InSb/GaSb quantum dots, J. Appl. Phys. 101, 124309.
Ferreira S.O., E.C. Paiva, G.N. Fontes, B.R.A. Neves (2001), Characterization of CdTe quantum dots grown on Si (111) by hot wall epitaxy, J. Cryst. Growth 231, 121.
Findlay P. C., C. R. Pidgeon, R. Kotitschke, A. Hollingworth, B. N. Murdin, C. J. G. M. Langerak, A. . van der Meer, C. M. Ciesla, J. Oswald, A. Homer, G. Springholz and G. Bauer (1998), Auger Recom-bination Dynamics of Lead Salts under ps Free Electron Laser Excitation, Phys. Rev. B 58 , 12908.
Glaser E. R., B. R. Bennett, B. V. Shanabrook, and R. Magno (1996), Photoluminescence studies of self-assembled InSb, GaSb, and AlSb quantum dot heterostructures, Appl. Phys. Lett. 68, 3614.
Grisar R., M. Tacke and H. Böttner (1992) Monitoring of Gaseous Pollutants by Tuneable Diode Lasers, (Kluwer Academic, Dordrecht).
Groiss, H., E. Kaufmann, G. Springholz, T. Schwarzl, G. Hesser, F. Schäffler, W. Heiss, K. Koike, T. Itakura, T. Hotei, M. Yano, T. Wojtowicz (2007), Size control and midinfrared emission of epitaxial PbTe/CdTe quantum dot precipitates grown by molecular beam epitaxy, Appl. Phys. Lett. 91, 222106.
Grundmann M., Nano-Optoelectronics (Springer Verlag, Berlin, 2002).
Harman T. C., PJ Taylor, MP Walsh, BE LaForge (2002), Quantum Dot Superlattice Thermoelectric Materials and Devices, Science 297, 2229.
Heiss W., T. Schwarzl, G. Springholz, K. Biermann and K. Reimann (2001), Above-room-temperature mid-infrared lasing from vertical cavity surface emitting PbTe quantum-well lasers, Appl. Phys. Lett. 78, 862-864.
Heiss, W., H. Groiss, E. Kaufmann, G. Hesser, M. Böberl, G. Springholz, F. Schäffler, K. Koike, H. Harada, and M. Yano (2006), Centrosymmteric PbTe/CdTe quantum dots coherently embedded by epitaxial precipitation, Appl. Phys. Lett. 88, 192109.
P04 Epitaxial lead salt nanostructures (Springholz)
Holy V., T.U. Schülli, R.T. Lechner, G. Springholz and G. Bauer (2005), Anomalous X-ray diffraction from self-assembled PbSe/PbEuTe quantum dots, J. Alloys and Compounds 401, 4–10.
Huang X., A. Stintz, C.P. Hains, C.P. Liu, G.T.Cheng, J. Malloy (2000), Efficient high-temperature CW lasing operation of oxide-confinedlong-wavelength InAs quantum dot lasers, Electron. Lett. 36, 41.
Katzir A., R. Rosman, Y. Shani, K. H. Bachem, H. Böttner, and H. M. Preier (1989), Tunable Lead Salt Lasers, in: Handbook of Solid State Lasers, ed. P. K. Cheo (Marcel Dekker, New York), pp. 228.
Kirstaedter M, N.N. Ledentsov, M. Grundmann, D. Bimberg, V.M. Ustinov, S.S. Ruvimov, M.V. Maximov, P.S. Kop'ev, Zh.I. Alferov U. Richter, P. Werner, U. Gösele, and J. Heidenreich (1994), Low threshold, large To injection laser emission from (InGa) As quantum dots, Electron. Lett. 30, 1416.
Lechner R. T., T. Schülli, V. Holy, G. Springholz, J. Stangl, A. Raab, T. H. Metzger and G. Bauer (2004), Ordering parameters of self-organized 3D quantum dot lattices determined by anomalous x-ray diffraction, Appl. Phys. Lett. 84, 885-888.
Leitsmann R. and F. Bechstedt (2007), Electronic-structure calculations for polar lattice-structure-mismatched interfaces: PbTe/CdTe (100), Phys. Rev. B 76, 1.
Leitsmann R., L.E.Ramos, F. Bechstedt, H. Groiss, F. Schäffler, W. Heiss, K. Koike, H. Harada, M. Yano (2006), Rebonding at coherent interfaces between rocksalt-PbTe/zinc-blende-CdTe, New J. Phys. 8, 317; and R. Leitsmann, L. E. Ramos, and F. Bechstedt (2006), Structural properties of PbTe/CdTe interfaces from first principles, Phys. Rev. B 74, 085309.
Leonard D., M. Krishnamurty, C.M. Reaves, S.P. Denbaar, P.Petroff (1993), Direct formation of quan-tum sized dots from uniform coherent islands of InGaAs on GaAs surfaces, Appl. Phys. Lett. 63, 3203.
Leute V, N J Haarmann, H M Schmidtke (1995), Solid state reactions in the quasiternary system (Cd, Pb) (S, Te), Zeitschrift für Physikalische Chemie 190, 253.
Liu X. and J. K. Furdyna (2004), Optical dispersion of ternary II–VI semiconductor alloys, J. Appl. Phys. 95, 7754 (2004).
Lugauer H.J., F. Fischer, T. Litz, A. Waag, D. Hommel, G. Landwehr (1994), Composition and tempe-rature dependence of the refractive index in CdMgTe epitaxial films, Semicond. Sci. Technol. 9, 1567.
Moison J. M., F. Houzay, F. Barthe, L. Leprince, E. Andre, and O. Vatel (1994), Self-organized growth of regu-lar nanometer-scale InAs dots on GaAs, Appl. Phys. Lett. 64, 196.
Motlan, E. M. Goldbys, and L. V. Dao (2002), Photoluminescence of GaSb self-assembled quantum dot layers grown by metalorganic chemical vapor deposition, J. Vac. Sci. Technol. B 20, 291.
Pinczolits M., G. Springholz, and G. Bauer (1998), Direct formation of self-assembled quantum dots under tensile strain by heteroepitaxy of PbSe on PbTe (111), Appl. Phys. Lett. 73, 250.
Preobrajenski A. B., K. Barucki, and T. Chassé (2000), Exploiting the Difference in Lattice Structures for Formation of Self-Assembled PbS Dots on InP(110), Phys. Rev. Lett. 85, 4337.
Pryor C. E, and M. E. Pistol (2005), Band-edge diagrams for strained III-V semiconductor quantum wells, wires and dots, Phys. Rev. B 72, 205311.
Raab A., and G. Springholz (2000), Oswald ripening and shape transitions of self-assembled PbSe quantum dots on PbTe (111) during annealing, Appl. Phys. Lett. 77, 2991.
Raab A., and G. Springholz (2002), Controlling the size and density of self-assembled PbSe quantum dots by adjusting the substrate temperature and layer thickness, Appl. Phys. Lett. 81, 2457.
Sandstrom, L.G. Lundqvist, S.H. Petterson, A.B. Shumate, M.S (1998), Tunable diode laser spectroscopy at 1.6 and 2 μm for detectionof Helicobacter pylori infection using 13C-urea breath test, IEEE J. Selected Topics Quantum Electron. 5, 1040.
Schubert D. W., M. M. Kraus, R. Kenklies, C. R. Becker, and R. N. Bicknell-Tassius (1992), Composi-tion and wavelength dependence of the refractive index in Cd1−xMnxTe epitaxial layers, Appl. Phys. Lett. 60, 2192.
Schülli T. U., R.T. Lechner, J. Stangl, G. Springholz, G. Bauer, M. Sztucki, T.H. Metzger (2004) Strain determination in multilayers by complementary anomalous x-ray diffraction, Phys. Rev. B 69, 195307.
Shchukin V. A., N.N. Ledentsov and D. Bimberg (2003), Epitaxy of Nano-Structures (Springer,Berlin).
Report – Project description
Schwarzl T., M. Eibelhuber, W. Heiss, E. Kaufmann, and G. Springholz, A. Winter and H. Pascher (2007), Mid-infrared high finesse microcavities and vertical-cavity lasers based on IV-VI semicon-ductor/BaF2 broad band Bragg mirrors, J. Appl. Phys 101, 093102-9.
Shields P. A., C. W. Bumby, L. J. Li, and R. J. Nicholas (2004), Mid-infrared electroluminescence from coupled quantum dots and wells, J. Appl. Phys. 96, 2725.
Simma M., D. Lugovyy, T. Fromherz, A. Raab, G. Springholz and G. Bauer (2006), Deformation po-tentials and photo-response of strained PbSe quantum wells and quantum dots, Physica E32, 123.
Simma M., T. Fromherz, A. Raab, G. Springholz, and G. Bauer (2006), Lateral photocurrent spectros-copy on self-assembled PbSe quantum dots, Appl. Phys. Lett. 88, 201105-17.
Springholz G. (2002), Molecular Beam Epitaxy of IV-VI Heterostructures and Superlattices, in: Lead Chalcogenides: Physics and Applications, ed. D. Khokhlov (Taylor and Francis).
Springholz G. (2008), Self-organized Quantum Dot Multilayer Structures, in: Handbook of Self Assembled Semiconductor Nanostructures for Novel Devices in Photonics and Electronics, ed. M. Henini (Elshevier, Oxford), p.1-60.
Springholz G. and V. Holy (2006), Stacking and Ordering in Self-Organized Quantum Dot Multilayer Structures Book chapter in : Springer Series on Nanoscience and Technology: Lateral Alignment of epitaxial quantum dots, ed. O. Schmidt (Springer-Verlag, Berlin).
Springholz G., M. Pinczolits P. Mayer, V. Holy, G. Bauer, H. Kang, and L. Salmanca-Riba (2000), Tuning of Vertical and Lateral Correlations in Self-Organized PbSe/Pb1-xEuxTe Quantum Dot Superlattices, Phys. Rev. Lett. 84, 4669.
Springholz G., T. Schwarzl and W. Heiss (2006), Mid-infrared Vertical Cavity Surface Emitting Lasers based on the Lead Salt Compounds, in: Mid-infrared Semiconductor Optoelectronics, ed. A. Krier (Springer-Verlag London), p. 265 – 302.
Springholz G., V. Holy, M. Pinczolits, G. Bauer (1998), Self-Organized Growth of Three- Dimensional Quantum-Dot Crystals with fcc-Like Stacking and a Tunable Lattice Constant, Science 282, 734.
Springholz, G., L. Abtin and V. Holy (2007), Determination of Shape and Composition of buried PbSe Quantum Dots using Scanning Tunneling Microscopy, Appl. Phys. Lett. 90, 113119.
Stepanov, E. V. (2002), Laser analysis of the 13C/12C isotope ratio in CO2 in exhaled air, Quantum Electron. 32 981-986.
Stier O., M. Grundmann, and D. Bimberg (1999), Electronic and optical properties of strained quan-tum dots modeled by 8-band k·p theory, Phys. Rev. B 59, 5688.
Sumpf B. S. Bouazzab, A. Kissela and H. -D. Kronfeldt (2000), Quantum Number Dependence of Lineshift Coefficients Induced by Collisions with Noble Gas Perturbers in the ν3 Band of NO2,J. Molec. Spectroscopy 199, 217.
Tacke M. (1995), New developments and applications of tunable IR lead salt lasers, Infrared Phys.Technol. 36, 447.
Tasco V., N. Deguffroy, A. N. Baranov, E. Tournié, B. Satpati, A. Trampert, M. S. Dunaevskii, and A. Titkov (2006), High-density, uniform InSb/GaSb quantum dots emitting in the mid-infrared region, Appl. Phys. Lett. 89, 263118.
Van de Walle C. G. (1989), Band lineups and deformation potentials in the model-solid theory Phys. Rev. B 39, 1871 – 1883.
Vurgaftman I., J.R. Meyer, L.R. Ram-Mohan (2001), Band parameters for III–V compound semicon-ductors and their alloys, J. Appl. Phys. 89, 5815.
Wei Su-Huai and S. B. Zhang (2002), Chemical trends of defect formation and doping limit in II-VI semiconductors: The case of CdTe, Phys. Rev. B 66, 155211.
Williamson, A. J., A. Zunger (1999), InAs quantum dots: Predicted electronic structure of free-standing versus GaAs-embedded structures, Phys. Rev. B 59, 5819.
Zhang S. B., Su-Huai Wei, and Alex Zunger (1998), A phenomenological model for systematization and prediction of doping limits in II–VI and I–III–VI2 compounds, J. Appl. Phys. 83, 3192.