Electronic Supplementary Material
An effective dual-solvent treatment for improving the thermoelectric
property of PEDOT:PSS with white graphene
Xiaodong Wang,1,2 Fanling Meng,1 Haitong Tang,1 Zhongmin Gao,1 Si Li,1 Fengxing Jiang,*,2 and
Jingkun Xu*,2
1 Key Laboratory of Automobile Materials, Ministry of Education, State Key Laboratory of
Inorganic Synthesis and Preparative Chemistry, College of Materials Science and Engineering, Jilin
University, Changchun, 130012, China.
2 Department of Physics, Jiangxi Science and Technology Normal University, Nanchang 330013,
China.
*The corresponding author, email: [email protected] (F. Jiang); [email protected] (J. Xu)
Figure S1 The stability comparison of BNNSs dispersed in different organic solvents
(DMSO, IPA,EG, and DMF) after 24 h.
Figure S2 TEM images of BNNSs for the parallel plane (a) and side plane (b).
Figure S3 UV-Vis-NIR spectra of (a) PEDOT:PSS and PEDOT:PSS-DMF solid thin films;
(b) the mother liquor of the filtration.
Figure S4 Thickness of PEDOT:PSS hybrid thin films with different contents of
BNNSs.