1. «Korona-2000» Ltd. (Ukraine). 2. OJSC «SILAN»,...

7400, Ukraine,

iev region, Brovary,

12 Zheleznodorozhnaya str.

el./Fax: +38 (044) 599-26-47

el.: +38 (044) 222-56-94

+38 (044) 599-26-64

E-mail: [email protected]

69009, Ukraine

Zaporozhye, 5 Teplichnaya str.

Tel/fax: +38(061) 222-09-73

Tel: +38 (061) 289-84-74

e-mail: [email protected]

Trade House Lakmar Ltd. was established in 2004. Our main business is

the import and export of high quality products and chemical raw materials

that meet international standards and requirements of todays market in

the segment of silicone, vinylester and epoxy products. All materials ex-

ported by our company to the European Union, have been pre-registered

under Regulation REACH.

Today, the range of products sold by Trade House Lakmar is about 300

items, including silicone enamels, silicone, heat-resistant and insulating

varnishes, epoxy, waterprooing liquids, emulsions, silicone liquids, and

more.

We are trusted by such companies as Knauf, Bayer, Wacker, Piccadilly,

OMYA, Atul, JSC Motor Sich, NNEGC Energoatom, Kievgorstroy,

PJSC ZAZ, PJSC Trade Alliance Nord, Corporation Volma , the cor-

poration TekhnoNIKOL and many others.

Trade House Lakmar Ltd. is an exclusive representative of such com-

panies as:

1. Korona-2000 Ltd. (Ukraine).

2. OJSC SILAN, Chemical plant in Dankov (Russia).

3. Hungarian Silicones (Hungary).

CONTENTS

VINYLESTER COMPOSITE MATERIALS

VINYLPLAST OF THE BRAND VINYLSKAT ............................................................................6


VINYLPLAST OF THE BRAND ANTIC .....................................................................................8

VINYLESTER COMPOSITE MATERIALS VINYLPLAST

OF THE BRAND ARMOPROK.........................................................................................................10

VARNISH KO-915B ..............................................................................................................................12

VARNISH KO-916A ..............................................................................................................................13

VARNISH KO-916K ..............................................................................................................................13

VARNISH KO-921 .................................................................................................................................14

VARNISH KO-922 .................................................................................................................................15

VARNISH KO-923 .................................................................................................................................16

VARNISH KO-978 .................................................................................................................................16

VARNISH KO-991-4 .............................................................................................................................17

VARNISH KO-916 .................................................................................................................................18

VARNISH -075 .................................................................................................................................19

VARNISH -85 ...................................................................................................................................20

VARNISH -815 .................................................................................................................................21

LIQUID PMS-5-1000 ...........................................................................................................................22

LIQUID 136-157 ..............................................................................................................................23

AQUAPROK-1 STANDARD .............................................................................................................24

AQUAPROK-1 CONCENTRATE ....................................................................................................26

AQUAPROK-1 SUPER CONCENTRATE ......................................................................................27

LIQUID GKZH-11K; GKZH-11N .......................................................................................................29

EMULSION SE-50/12 ..........................................................................................................................31

EMULSION ME-50/42 ........................................................................................................................32

EMULSION MSE-50/43 ......................................................................................................................33

EMULSION KE10-01 ...........................................................................................................................34

EMULSION GKE 50-94M ...................................................................................................................35

ETHYLSILICATE 40 ...............................................................................................................................37

BINDER KP-1 .........................................................................................................................................38

AQUAPROK-3 .......................................................................................................................................39

RESIN ED-16 ..........................................................................................................................................40

RESIN ED-20 ..........................................................................................................................................41

CHEMICAL-RESISTANT

VINYLESTER MATERIALS

ETHYLSILICATES

EPOXY PRODUCTS

POLYMETHYLSILICONE

LIQUIDS

ELECTRIC INSULATING

VARNISHES

EMULSIONS

HEAT-RESISTANT

VARNISHES

CONTENTS

RESIN E-40 .............................................................................................................................................41

ENAMEL EP-5K .....................................................................................................................................42

ENAMEL EP-525 ................................................................................................................................43

ENAMEL EP-574 ................................................................................................................................44

ENAMEL EP-5123 ..............................................................................................................................46

ENAMEL QUR-5 ....................................................................................................................47

FILLER EP-0010 ..................................................................................................................................48

COMPOSITION EKOPOL ................................................................................................................50

COMPOSITION POLYPOL ..............................................................................................................51

EXTERIOR ENAMEL KO-168K ..........................................................................................................53

HEAT-RESISTANT ENAMEL KO-811 .............................................................................................55

HEAT-RESISTANT ENAMEL KO-813 ...............................................................................................56

HEAT-RESISTANT ENAMEL KO-814 ...............................................................................................57

HEAT-RESISTANT ENAMEL KO- 828 ............................................................................................57

ENAMEL 5102K ............................................................................................................................58

PRIMER GF-0119 .................................................................................................................................61

PRIMER GF-021 ....................................................................................................................................62

ENAMEL PF-101 ................................................................................................................................63

ENAMEL PF-115 ................................................................................................................................64

MASTIC IZOLON ..................................................................................................................................66

MASTIC ZHKMA ...................................................................................................................................67

MASTIC ZHKMG ...................................................................................................................................68

RUBBER SKTN ......................................................................................................................................69

PAINT WD-AK-111 ...............................................................................................................................70

PAINT WD-KCH-183 ............................................................................................................................71

POTASSIUM HYDROXIDE ..................................................................................................................73

METHYL SILICA GEL ...........................................................................................................................75

FLOOR COATING

EPOXY PRODUCTS

SILICON ENAMELS

ENAMELS AND PRIMERS BASED

ON ALKYD VARNISH

RUBBER AND

RUBBER MASTIC

WATER-DISPERSED PAINTS

POTASSIUM HYDROXIDE

METHYL SILICA GEL

6

Features

Application

Coatings are resistant to inluence of:


VINYLPLAST OF THE BRAND VINYLSKAT

Anti-abrasive, anti-wear and corrosion-resistant coating based on vinylester resin.

Vinylplast is designed for corrosion prevention of equipment (water treatment systems, capacitive equipment and others), constructions and installations includ-ing luid- and sulphur-reinement and for production of coatings operated in ag-gressive environments.

hightemperature(upto230); inorganicacid(sulfuricacid,sulfurousacid,hydrochloricacid,hydroluoricacid and others); alkali; desalinatedwater,servicewater,ionizedorseawater; combustion gases (from combustion of coal, fuel oil, sulfur-containing compounds); sulphurdioxide,carbondioxide,nitrogenoxide;hydrogenchloride.

After polymerization it is formed a durable coating of high density with high corro-sion resistance and solidity.

The material Vinylplast is used for internal and external protection of tanks, cooling stacks, pipings, valves, neutralization tanks, boxes for batteries and capacitors, systems for water processing, fan shrouds, lining the basements, ion-exchange ilters of sulphur-cleaning machines (gas lues), metal pipes, scrubbers, absorbers, etc.

CONTENTSCHEMICAL-RESISTANT VINYLESTER

MATERIALS

7

Surface preparation:

Physical and mechanical parameters

Colour

Name of parameter and unit of measure Standard

Density, g/cm3 1,2 1,5

Adhesive strength, MPa at least 7

Strength at impact, m at least 60

Bending strength, P 40-60

Ultimate tensile strength, MPa 20-25

Resistance to abrasion (wear), micron 35-40

Resistance to liquid corrosive media at temperature (505),h at least 10

Heat resistance, at least 250

Green and grey of various shades.

Preparation of metal surface:

cleanbysand-blastingmethod(degreeofpuriicationofthemetalsurfacemustbe no lower than second in accordance with state standard GOST 9.402-80, or not lower than St 3 or Sa 2,5 according to ISO 8501-01). If before coating passed more than 6 hours after surface preparation, the treatment must be repeated; degreasewithorganicsolvents.

Preparation of concrete surface:

clean thoroughly and if necessary smooth out the surface (cracks, holes, roughness) with appropriate concrete repair mortar or building mortar, prepared on basis of the material Vinylplast of the mark Vinylskat. The prepared surface should be smooth, even, without grease, moisture content of the concrete in the surface layer into depth to 20 mm should be no more than 4%. Roughness class is at least 3R.

It consists of primer coat and protective composition.The primer coat Vinylplast consists of half-inished products (suspension of pigments and illers in the resin solution with the functional additives) and hardener (organic peroxide).

The Vinylplast composition of mark Vinylskat consists of half-inished product (a suspension of pigments and illers in the resin solution with the functional additives, illed with glass scales of special type) and a hardener organic peroxide.

introduce the hardener in a half-inished product immediately before use in the ratio of 2,5-3,0 parts of hardener by weight (depending on ambient temperature) to 100 parts of basis by weight, or according to instructions in the passport; mixthoroughlyfor3-5minutessincepreparation; usewithin10minutesafterpreparation.

introduce the hardener in a half-inished product immediately before use in the ratio of 1,5-3,0 parts of hardener by weight (depending on ambient temperature) to 100 parts of basis by weight, or according to instructions in the passport; mixthoroughlyfor3-5minutessincepreparation; usewithin10minutesafterpreparation.

Minimal temperature of environment, working compositions and protected surface at performance of works should be higher than dew point by 3 C, but not lower than 10 C and not higher than 35 C. The relative humidity should not be higher than 70%.

Composition of protective system of coatings

Primer coat preparation:

Preparation of composite protective composition:

Coating conditions

8

applytheprimerusingpaintbrush,rollerorairlessspray; after24hours,applytheprotectivecompositionwithapaintbrush,roller,trowel or airless spray. Apply each subsequent layer not earlier than 24 hours after the previous application. The number of applied layers varies from 2 to 6, depending on operating conditions and the required service life; after 24 hours apply 1-2 sealing layers using the paint brush, roller, trowel or airless spray. Apply each subsequent layer not earlier than 24 hours after the previous application.

primerfrom0,17kg/m2; protectivecompositionfrom0,36kg/m2 for one layer; protectivecompositionforsealinglayerfrom0,26kg/m2 for one layer;

The coating in cured state is non-toxic and ireproof.

Shelf life: 6 months.

TU U 24.3-33444644-002:2006 amendment 1.

Coating:

Material consumption:

Safety information

Resistance of the coating:


Features

Application

Protective systems consisting of a binder based on vinylester with inorganic illers.

For protection of equipment, metal and concrete structures and build-ings that are subject to atmospheric corrosion in combination with exposure to aggressive media.

Coatings are resistant to mechanical shock and vibration exposure, UV radiation, abrasion, as well as to the inluence of: inorganicacidsandalkalis: waterdesalinated,technical,ionized,sea: oxides (gases) sulfur, nitrogendioxide,hydrogenchloride, ammonia, carbon dioxide, oxides of phosphorus; Petroleumproductsgasoline,dieselfuel,fueloil,petroleum,mineraloils.

CHEMICAL-RESISTANT

VINYLESTER

MATERIALS


VINYLPLAST OF THE BRAND ANTIC





Bending strength, P at least 40

Ultimate tensile strength, MPa at least 20

Resistance to abrasion (wear), micron 20-25

Resistance to liquid corrosive media at temperature (505),h at least 10


9

Colour


Green, brown.


cleanbysand-blastingmethod(degreeofpuriicationofthemetalsurfacemust be not lower than second in accordance with state standardGOST 9.402-80, or not lower than St 3 or Sa 2,5 according to ISO 8501-01). If before coating passed more than 6 hours after surface preparation, the treatment must be repeated; degreasewithorganicsolvents.


cleanthoroughlyand ifnecessarysmoothoutthesurface(cracks,holes, roughness) with appropriate building mortar. The prepared surface should be smooth, even, without grease, moisture content of the concrete in the surface layer into depth to 20 mm should be no more than 4%. Roughness class is at least 3R.

It consists of primer coat and protective composition.The Vinylplast primer consists of half-inished product (a suspension of pigments and illers in the resin solution with the functional additives) and a hardener organic peroxide).

The material Vinylplast of brand ntic is a suspension of pigments, illers in the solution of resin with functional additives.

introduce thehardener inahalf-inishedproduct immediatelybeforeuse in the ratio of 2.5-3.0 parts of hardener by weight (depending on ambient temperature) to 100 parts of basis by weight, or according to instructions in the passport; mixthoroughlyfor3-5minutessincepreparation; usewithin10minutesafterpreparation.

Supplied ready for use.


apply1-2layersoftheprimerusingpaintbrush,rollerorairlessspray; after 24 hours, apply the protective composition with a paint brush, roller, trowel or airless spray. Apply each subsequent layer not earlier than 24 hours after the previous application. The number of applied layers varies from 2 to 4, depending on operating conditions and the required service life.

primerfrom0,17kg/m2; protectivecompositionfrom0,25kg/m2 for one layer.



U U 24.3-33444644-002:2006 amendment 1.

Composition of protective system

of coatings


Preparation of protective composition

Coating conditions

Coating:


Safety information

10

Features


VINYLPLAST OF THE BRAND ARMOPROK

Internal laminated protective coatings and insulation of stationary metal tanks for storing petroleum products

For protection against corrosion of metal and concrete structures (tanks, reservoirs, pipelines, appliances, walls and loors) as a reinforced protective isolation. For internal reinforced protective insulation of the bottom and irst zone instead of replacement of destroyed metal tank bottom with new metal bottom, also for reinforcement of metal bottoms, that have come unusable due to corrosion thinning.

For corrosion protection, and strengthening the walls of the equipment, main and technological pipelines, including working under pressure, as a composite reinforcing ties.

diluteandconcentratedmineral acids (hydrochloric,nitric,phosphoric, formic, acetic, etc.); diluteandconcentratedalkalis; saltsandtheirsolutions(sulfates,nitrates,chlorides,hypochlorites,etc.); desalinated,technical,ionized,seawater; petroleumandpetroleumproducts(gasoline,diesel,fueloil); organicsolvents(alcohols,xylene,etc.).

After polymerization, it is formed a durable coating of high density with high corro-sion resistance and durability.

Application

Coatings are resistant to inluence of:


Colour


Green, brown, grey.


cleanbysand-blastingmethod(degreeofpuriicationofthemetalsurfacemust be not lower than second in accordance with state standard GOST 9.402-80, or not lower than St 3 or Sa 2,5 according to ISO 8501-01). If before coating passed more than 6 hours after surface preparation, the treatment must be repeated; degreasewithorganicsolvents.

CHEMICAL-RESISTANT

VINYLESTER

MATERIALS





Bending strength, P at least 190

Ultimate tensile strength, MPa at least 73

Resistance to abrasion (wear), micron no more 42

Resistancetoliquidcorrosivemediaattemperature(505),h at least 10


11

Composition of protective system

of coatings


cleanthoroughlyandifnecessarysmoothoutthesurface(cracks,holes,roughness) with appropriate building mortar. The prepared surface should be smooth, even, without grease, moisture content of the concrete in the surface layer into depth to 20 mm should be no more than 4%. Roughness class is atleast 3R.

It consists of primer coat and protective composition.The Vinylplast primer consists of half-inished product (a suspension of pigments and illers in the resin solution with the functional additives) and a hardener organic peroxide.

The composition Vinylplast of the brand Armoprok consists of half-inished product (a suspension of pigments and illers in the resin solution with the functional additives) and a hardener organic peroxide.

introducethehardenerinahalf-inishedproductimmediatelybeforeuseinthe ratio of 2.5-3.0 parts of hardener by weight (depending on ambient temperature) to 100 parts of basis by weight, or according to instructions in the passport; mixthoroughlyfor3-5minutessincepreparation; usewithin10minutesafterpreparation.

introducethehardenerinahalf-inishedproductimmediatelybeforeuseinthe ratio of 1.5-3.0 parts of hardener by weight (depending on ambient temperature) to 100 parts of basis by weight, or according to instructions in the passport; mixthoroughlyfor3-5minutessincepreparation; usewithin10minutesafterpreparation.


applytheprimerusingpaintbrush,rollerorairlessspray; after24hoursrepairthesurface-illindefects(sinks,cracks)withrepairmortar, prepared on the basis of the material Vinilplast of the brand Armoprok; after24hoursapplythesystemofprotectivelaminateconsistingofsequentially stacked on the material Vinylplast brand Armoprok 2 layers of glass iber and a second layer of glass veil. Apply each subsequent layer not earlier than 24 hours after the previous application: after24hoursapply1-2sealinglayersofVinylplast of the brand Armoprok protective composition using paint brush, roller, trowel or airless spray. Apply each subsequent layer not earlier than 24 hours after the previous application.

primerfrom0,17kg/m2; protectivecompositionforgluingglassmaterialsfrom1,06kg/m2 per one layer; protectivecompositionforsealinglayerfrom0,26kg/m2 per one layer.



U U 24.3-33444644-002:2006 amendment 1.


Preparation of protective composition:

Coating conditions

Coating:


Safety information

12

fELECTRIC INSULATING

VARNISHES

Features

Application:

VARNISH KO-915B

Solution of polyether resin-modiied organopolysiloxane resin in toluene.

KO-915Bshowsgoodheatresistance,highdielectriccharacteristics,goodadhe- sive and insulating capacity. KO-915Bservesforpreparationofheat-andhumid-resistantelectricinsulatingma- terials which are used in manufacture of class H electrical machines and apparatus. KO-915B is also used in themanufacture of glass fabrics, glass iber- insulated wires, insulating enamels.

Physical and chemical properties

Health and safety information

Weight of non-volatiles, % 65 2

Viscosity, s 15 - 40

Dryout time, 3rd degree, (2005)C, mins, max. 35 - 75

Thermo elasticity (2003) C, hrs, min. 150

Viscosity by viscometer VZ-246, oriice 4mm, s 30 - 70

Dielectric properties Test conditions

R,(17-35)45-75%

R,M(180)

13

Homogenous clear solution of polyether-modiied organopolysiloxane resin in toluene.

Varnish KO-916A is designed for production of iberglass- insulated winding wires and heat-resistant wires and cables with iberglass prooing. The KO-916A coating shows high durability, weather and moisture resistance, resistance to attack of oil, heat, and gasoline.

Features

Applications:

VARNISH KO-916A



Viscosity, 20 C, by viscometer VZ-246 with

oriice 4 mm, s30 - 60

Dryout time, 3rd degree, (2005)C, mins, max. 15

Weight of Si- bound hydrogen,%, max. 0,0018

Thermo elasticity, 200C, hrs, min. 50

Hardness by pendulum device ME-3, 20, min. 0,6

Hardness by pendulum device ME-3, 180, min. 0,2

Optical density, max. 0,5


(15-35)45-75%

M(200)

14


The polymerized varnish coat is nontoxic, ire-safe.

Guaranteed shelf life: 6 months.

6-02-1-012-79 amendment 1-5.


Varnish KO-921 is a clear homogenous solution of polymethylphenylsilxane resin in organic solvents. Polymethylphenylsiloxane resin is obtained by hydrolytic condensation of phenyltrichlorosilane and dimethyldichlorosilane with further polymerization.

Varnish KO-921 is distinguished by its lowdrying temperature, good dielectric properties, moisture and heat resistance. Theproduct serves for impregnationofglasswindingofwires andcables. It is alsousedasimpregnatingandcoatingvarnish,operatingat250C. The product is widely used for protection of electric machines and apparatus from mold and fungi. Infoodindustry,thevarnishisusedasreleaseagentformetalformsforbaking meat as well as protective coat for metal forms for baking bread and biscuits.

Features

ELECTRIC INSULATING

VARNISHESVARNISH KO-921

Applications




oriice 4 mm, s45-65

Dryout time, 3rd degree, (2005)C, mins, max. 15

Thermo elasticity, (2003)C, hrs, min. 50


Cementing capacity of varnish coat, 20C, N, min. 294 (30)


R,(15-35)45-75%

R,M(200)

15




oriice 4 mm, s17-27

Dryout time, 3rd degree, (2005)C, mins,

max.15

Weight, of Si-bound hydrogen, %, max. 0,001

Thermo elasticity, 250 C, hrs, min. 100



R,(15-35)45-75%

R,M(200)

16

Varnish KO-923 is a clear, homogenous solution of organopolysiloxane resin in toluene obtained by hydrolytic co-condensation of phenyltrichlorosilane and dimethyldichlorosilane with further polymerization.

VarnishKO-923possesseshighdielectricproperties,goodadhesiveandimpreg- nating ability. Varnish KO-923 is used for impregnation of winding of electric machines and apparatusoperatingat180-220Cunderhighhumidityconditions. It also serves for preparationof protectiveheat-resistant enamels continuously operatingat80-220Candat250-300Cforashorttime. VarnishKO-922iswidelyusedasantirustcoatingformetalsurfaces.

Features

VARNISH KO-923

Applications




oriice 4 mm, s

17-27

Dryout time, 3rd degree, (2005) C, mins, max. 30

Cementing capacity, (15-35) C, N, min. 206

Thermo elasticity, 220 C, hrs, min. 100


Color by iodine scale, max. 0,5


R,(15-35) 45-75%

R,M(180)

17




U U 24.3-00203625-093-2002.

Guaranteed shelf life:12 months. U 6-02-753-78 amendment 1-5.




Viscosity, s 16-25

Dryout time, 3rd degree, 200 C, mins, max. 30

Jelliication, (1502)C, s 40-80

Weight, of Al, % 0,07 - 0,08

Cementing capacity of varnish coat, N, min. 196


R,(15-35) 45-75%

R,M(180)

18

Homogenous clear solution of polyether-modiied organopolysiloxane resin in ethyl cellosolve.

Varnish KO-916 is used for varnishing of electrical steel.

Features

VARNISH KO-916

Applications

ELECTRIC INSULATING

VARNISHES


Conventional viscosity, s 45-65

Dryout time, 3rd degree, (2005)C, mins,

max.

15

Thermo elasticity, (2005)C, hrs, min. 50

Hardness by pendulum device ME-3, (205),

min.

0,5

Hardness by pendulum device ME-3,

(1802), min.

0,2

Optical density, at 400 nm, max. 0,6


R,(15-35)45-75%

R,M(180)

19

f

VARNISH -075

HEAT-RESISTANT

VARNISHES

Light-yellow to dark-brown transparent liquid, a solution of polyester-modiied polymethylphenylsiloxane resin in toluene.

Preparationof theheat-resistant enamel KO-835.The latter is prepareddirectly before use by mixing 94 parts by weight of the varnish and 6 parts by weight of aluminium powder. The enamel is designed for parts operating at temperature of about 500 C. Protectionofseparators,gastrapswiththeitting,cyclonesettlersinoil-ields. Corrosionpreventionofexternalsurfaceofgasducts,chlorinators,steamandgas turbines, ejectors, diferent elements of agricultural machines, air drying apparatus, chemical catching equipment, equipment in by-product coke production. Protectionofcarradiatorsaswellasotherelementsandequipmentoperatingat 350-400 C for a long time. Corrosionpreventionof internalsurfaceofsteam-water tanksoperatingat150- 160 C. Sizing and dressing of artiicial fur; improvement of resistance of protective clothing to attack by acids; impregnation of ilter fabrics to increase serviceability, heat and wear resistance. Releasecoatingintheproductionofglassandiberglassplastics;acomponentof parting paints. CombinationofthevarnishKO-075withpentaphthalic(perchlorovinyl)nitrocellu- lose enamels provides improvement of the ilm strength, water, heat and light resistance, water repellency, gloss and hardness.

Features

Applications

20

Fraction of total mass of nonvolatiles, % 37 3

Acid number, mg KOH/g of varnish max. 6,0


Physical and chemical parameters



U 6-02-1-030-91 amendment 1-4.

Polymerized varnish ilm is non-toxic and ireproof.


GOST 11066-74.


Safety information

Polyphenyldimethylsiloxane resin solution in toluene modiied with solution of po-lybutene methacrylic resin in a mixture of acetone, ethyl acetate and butyl acetate or xylol.

As a varnishWood products without polishing, and also for restoration of damaged paint coating. As heat-resistant enamel (the enamel is obtained by mixing of varnish with an aluminium powder in the ratio 100:5).

In engineering (exhaust pipes, injectors of tracked vehicles, parts of boilers, chimneys and wire ends).

Varnish featuresIncreasedthermal(metalproducts,operatedat300-350Cforalongtime),water-and petrol-resistance.

Features

HEAT-RESISTANT VARNISH -85HEAT-RESISTANT

VARNISHES


Funnel viscosity, 12-17

Mass content of nonvolatile substances, % 15-17

Drying time of varnish ilm to degree 3 at temperature (205)C, hours, no more

3

Acid number, mg KOH / g of varnish Not more than 3

21


The varnish ilm in cured state is not toxic and ireproof.


GOST 11066-74.

Safety information


Funnel viscosity by viscosimeter -246 with nozzle diameter 4 mm, 10-13

Mass content of nonvolatile substances, % 33-37

Acid number, mg /g of varnish No more than 10

Dryingtimeofvarnishilmtodegree3at(150+2)0,h No more than 1

The solution of polyphenyl siloxane resin modiied with glyptal varnish, in toluene or acid.

For the manufacture of heat-resistant enamels, obtained by mixing of varnishes with the aluminum powder PAP-2. The enamels are designed for coating of metal products exposedtotemperaturesupto400-500foralongtime.

Transparent liquid from light-yellow to brown color.

Features

HEAT-RESISTANT VARNISH -815HEAT-RESISTANT

VARNISHES

Applications

Color

22

LIQUIDS PMS-5-1000

POLYMETHYLSILICONE

LIQUIDS

Features

Application

Polymethylsilicone liquids are blend of polymers with linear and branched structure.

Fluid grade Flash point, Kynematic viscosity, cSt

PMS-5 min. 116 4,5 - 5,6

PMS-10 min. 172 9,2 - 10,8

PMS-20 min. 200 18 - 22

PMS-40 min. 200 36 - 44

PMS-50 min. 220 45 - 55

PMS-100 min. 305 95 - 105

PMS-200 min. 316 192 - 208

PMS-300 min. 310 290 - 310

PMS-400 min. 315 385 - 415

PMS-500 min. 316 480 - 520

PMS-1000 min. 310 950 - 1050

LIQUIDPMS5-10areusedasdampingliquidsandthermalliquids(bothlow-and hightemperature) for instrumentation. LIQUIDPMS20-40arecommonlyusedasdamping,hydraulic,partingliquidsfor instrumentation as well as grease base. LIQUIDPMS50-200areusedasdamping,hydraulic,partingliquidsaswellasad- ditives in polishing liquids and a variety of household chemical goods. LIQUIDPMS300-400areusedasabaseofpetrolatumpaste.Water-basedemulsions of these liquids are used as release agents in production of general mechanical rubber goods, plastic goods, and rubbers , also in production of dielectric pastes and petroleum jellies , and as damping liquid. LIQUIDPMS500-1000areusedasdampingliquid.

23

Application LIQUIDPMS100Risusedasabaseconstituentoflow-temperaturegreases,refriger- ant, and low-temperature liquids for a variety of instrumentation. LIQUIDPMS200-Aisusedasfoaminhibitingagentforpetroleumoilsandprinting inks in printing industry as well as parting agent in tire industry. LIQUIDPMS-200,300andtheemulsiononthebaseofPMS-400areallowedtouse in food industry.

Kynematic viscosity, St, 20C 4,5 1050 depending upon grade of liquids

Flash point (o.c.), 116 316 depending upon grade of liquids

Freezing temperature, minus 100 minus 60 depending upon grade of liquids

Boiling point 0,13-0,5 kPa residual pressure,

C:

PMS 5-10 170 - 250

PMS 10-40 more than 250

PMS 50-1000 more than 300

Content of silicon, % 35,5 - 38,5 depending upon grade of liquids

Self-ignition temperature, 330 - 400 depending upon grade of liquids

Inlammation limits of vapor in air, , lower 128 - 214 depending upon grade of liquids

Inlammation limits of vapor in air, , upper 256 - 297 depending upon grade of liquids

Density, g/cm3, at 20 0,91 0,98

Density, g/cm3, at minus 60 1,03 - 1,04 by viscosities > 200 cSt

Solubility, %, in water, less than 0,2

Solubility, %, in aromatic and chlorinated

hydrocarbons100

Solubility, %, in spirit, acetone full by PMS 510

Heat conductivity 20, watt/m. 0,167


Polymethylsilicone luids are inert, explosion-proof, produces no poisonous action to skin and conjunctiva.


GOST 13032-77 amendment 1-3.


Oligo methyl siloxane hydride.

forwaterprooingthesurfaceofconcrete,brick,asbestoscementandceramics,gypsum and other mineral surfaces (as a solution in organic solvents). asawater-repellentadditiveinrepairingresidential,publicandindustrialbuildings and structures; intheproductionofireextinguishingpowdersbasedonammoniumphosphate for the preparation of anti-adhesive lubricants in the manufacture of iberglass products.

Features

Application

POLYMETHYLSILICONE

LIQUIDS

LIQUIDS GKZH 136-157(analog Silres BS94)

24

The surface of construction materials treated with liquid do not absorb moisture and is not destroyed by the cycles of freezing and thawing of water, which increases the life of the material.

Water-repellent coating does not change the appearance of the material, does not prevent the normal air ventilation within the construction, reduces dirt retention, and prevents the reduction of heat-insulating properties of the material, resistant to sunlight. The treated surface is not exposed to the damaging efects of mosses and lichens.


Appearance Colorless or light yellow liquid

Mechanical impurities not presented

Mass fraction of active hydrogen, % 1,5 -1,6

Kinematical viscosity, cSt 15,0 - 30,0

The reaction of medium (pH of aqueous extract) 6,0 - 7,0

Water-repelling ability, h a 3,0

Densityattemperature(25+0,5),g/sm3 0,990 -1,010

Therefractiveindexattemperature(25+0,5) 1,3960 -1,4100

Mass fraction of volatile substances, not more than, % 3

Remove dust, dirt, grease, laitance and other contamination by any mechanical way.

Dilute the liquid with organic solvent (preferably using acetone) in the ratio 1 part by weight of liquid GKZH-136-157M for 10 parts by weight of solvent. Mix thoroughly.

Apply a working composition on dry surface until the termination of absorption. Do not allow lowing and leaving drops. Do not work when raining, and outside temperaturelowerthan5.

Ceiling brush, roller, spraying.

Consumption of the working composition 200-350 g/m2.

Physiologically harmless.


TU U 24.6-33444644-007:2009, amendment 1.

Characteristics of the material


Surface preparation prior to water-repellency treatment

Preparation of the working composition

Coating

Application methods:

Consumption

Safety information:

Water solution of potassium methylsiliconate, ready for use.

Most of building materials of mineral origin have pores, so they have greater moisture absorption (40%). Moistened materials signiicantly reduce the thermal insulation properties. Thus, the moistening of normal brick for just 10%, increases its thermal conductivity in 1,5 times.

Features

WATER-REPELLENT AGENT AQUAPROK-1

STANDARD

POLYMETHYLSILICONE

LIQUIDS

25

FeaturesAlternate freezing and thawing of water in the pores of stone materials, alternate wetting and drying, the disjoining efect of water ilms on the micro particles of these materials, chemical inluences of aqueous solutions of salts, acids, alkalis, inally resulting to a strength reduction, are the main damaging factors decreasing the durability of constructions.

One of the most reliable, easy and cost saving ways of signiicant increasing the quality and durability of building materials is their water-repellency treatment with Aquaprok liquid.

The application of the Aquaprok liquid in exterior water-repellency treatment when building and repair works will allow:

to prolong the service life of buildings in 3 5 times, preventing fungi emergence and growth; to increase the frost resistance of buildings in the 2 3 times and corrosion resistance in 1,5 2 times; to reduce the water absorption in 1,5 times; to save heat by reducing of heat-transfer through the walls and ceilings; to avoid repeated elorescence; to improve the antisplash properties.

for surface treatment of brick, concrete, foam concrete, shellstone, plastered surfaces, limestone, asbestos cement, slate, tile, marble, gypsum products, and other porous materials; for bulk handling when prepare plaster, lime, cement, concrete solutions.

Treated materials have reduced water permeability and water absorption, increased frost-resistance and thermal insulation properties, anti-mold and anti-moss protection. At the same time natural qualities of materials are preserved.

Description of property and measuring unit Standard

Appearance Transparent or slightly turbid liquid

Densityattemperature(20,0+0,5),g/sm3 1,02 1,035

Mass fraction of solids, % 3,0 5,0

Transparent liquid.

Thoroughly clean surface of dirt, exfoliated areas of plaster, then blow dust with air (or sweep mechanically). If necessary, smooth the surface (issures, sinks, irregularities) with appropriate building solution.

Inlict on dry surface until the termination of absorption. Do not allow sagging and leavingdrops.Donotworkwhenraining,andoutsidetemperaturelowerthan5.

Note: reprocessing of the dry layer can lead to a white elorescence.

Brush, roller or spray.

Consumption of working solution depends on porosity of treated material and it averages 350 ml per 1 m2.

Application

Color

Surface preparation(when surface treatment)

Inliction (when surface treatment)

Inliction techniques (when surface treatment)

Consumption on a lat surface

(when surface treatment)

Physical and mechanical properties

26

When preparation of building solutions and concrete the agent is to be introduced together with mixing water in amount of 0,75-1,5 % by weight of the binder cement or lime.

Products are delivered in plastic canisters volumes of the 3L, 5L and 10L. Packaged in stretch ilm on euro pallets.

The agent is non-toxic, ire and explosion proof, but it has alkaline properties. When working, wear rubber gloves, goggles, spray from windward side, use respirator.

Shelf life: 12 months.U U 24.6-33444644-012:2010.

Application (when bulk treatment)

Packaging:

Safety information

Water solution of potassium methylsiliconate.


Alternate freezing and thawing of water in the pores of stone materials, alternate wetting and drying, the disjoining efect of water ilms on the micro particles of these materials, chemical inluences of aqueous solutions of salts, acids, alkalis, inally resulting to a strength reduction, are the main damaging factors decreasing the durability of constructions.



to prolong the service life of buildings in 3 5 times, preventing fungi emergence and growth; to increase the frost resistance of buildings in the 2 3 times and corrosion resistance in 1,5 2 times; to reduce the water absorption in 1,5 times; to save heat by reducing of heat-transfer through the walls and ceilings; to avoid repeated elorescence; to improve the antisplash properties.

for surface treatment of brick, concrete, foam concrete, shellstone, plastered surfaces, limestone, asbestos cement, slate, tile, marble, gypsum products, and other porous materials; for bulk handling when prepare plaster, lime, cement, concrete solutions.


Features

Application


CONCENTRATE

POLYMETHYLSILICONE

LIQUIDS

27


Packaging

Safety information





Transparent liquid.


Prepare working solution in proportion 1 liter of agent for 3 liters of water, in quantity necessary for 12 hours of work.


Note: Violation of technology for preparation and use of the working solution, as well as the reprocessing of the dry layer can lead to a white elorescence.



When preparation of building solutions and concrete the agent is to be introduced together with mixing water in amount of 0,1-0,2% by weight of the binder cement or lime.

Products are delivered in plastic canisters volumes of the 3L, 5L and 10L.Packaged in stretch ilm on euro pallets.


Shelf life 12 months. Technical standard U U 24.6-33444644-012:2010.


Color


Preparation of working solution






POLYMETHYLSILICONE

LIQUIDS


SUPER CONCENTRATE

FeaturesConcentrated water solution of potassium methylsiliconate.


28

Alternate freezing and thawing of water in the pores of stone materials, alternate wetting and drying, the disjoining efect of water ilms on the micro particles of these materials, chemical inluences of aqueous solutions of salts, acids, alkalis, inally resulting to a strength reduction, are the main damaging factors decreasing the durability of constructions.



toprolongtheservicelifeofbuildingsin35times,preventingfungiemergence and growth; to increase the frost resistance of buildings in the 2 3 times and corrosion resistance in 1,5 2 times; toreducethewaterabsorptionin1,5times; tosaveheatbyreducingofheat-transferthroughthewallsandceilings; toavoidrepeatedelorescence; toimprovetheantisplashproperties.

for surface treatment of brick, concrete, foam concrete, shellstone, plastered surfaces, limestone, asbestos cement, slate, tile, marble, gypsum products, and other porous materials; forbulkhandlingwhenprepareplaster,lime,cement,concretesolutions.






Transparent liquid.


Prepare working solution in proportion 1 liter of agent for 10 liters of water, in quantity necessary for 1-2 hours of work.


Note: Violation of technology for preparation and use of the working solution, as well as the reprocessing of the dry layer can lead to a white elorescence.


Application


Color


Preparation of working solution (when surface treatment)



29


When preparation of building solutions and concrete the agent is to be introduced together with mixing water in amount of 0,1-0,2% by weight of the binder cement or lime.

Products are delivered in plastic canisters volumes of the 3L, 5L and 10L. Packaged in stretch ilm on euro pallets.


Shelf life : 12 months. Technical standard U U 24.6-33444644-012:2010.




Packaging:

Safety information

Water solution of sodium or potassium methyl siliconate.

For surface treatment (GKZH-11K is applied) in order to increase the useful life of buildings and structures, as the surface treated with water-repellent liquid almost does not absorb water and is not polluted with precipitation. The surface water repellent treatment of coatings is efective within 45 years.The coatings that can be treated are brickwork, wall panels, cement screeds and con-crete, limestone, porous rock, slate, tile, plaster coating.

For volumetric treatment (GKZH-11K and GKZH-11N are applied):

in thepreparationofplaster,cement,concretesolutions, that reducestheirwater absorption and permeability, increases the plasticity of solutions, the strength of plaster and screed, increases frost resistance of the concretes of normal hardening regardless of their composition and the type of binder. in the production of asphalt and bituminous mixtures. The addition of water- repellent liquids increases water-repellent properties of the materials, neutralizes acids contained in them, increases frost resistance of asphalt coatings and reduces their cracking.

Name of parameter and unit

of measure

Standard

Liquid GKZH 11N of grade B Liquid GKZH 11N of grade V

Appearance and colour Liquid from colorless to light brown color. May be turbid

Liquid from light yellow to brown

Density at temperature

(20+0,5) , g/m3 1,17 1,30 1,14 1,30

Alkalinity in terms of NaOH, % 13 -17 Not more than 17

Mass fraction of solids, % 25 35 23 33

Water-repellent ability Passed the test Passed the test

Features

Application

POLYMETHYLSILICONE

LIQUIDS

WATER-REPELLENT LIQUIDS GZH-11

AND GZH-11N (GZH-11 - analogs BS16)

Physical and mechanical parameters of liquid

GKZH-11 N

30

Name of parameter and

unit of measure

Standard

Liquid GKZH 11N of grade B Liquid GKZH 11N of grade V

Appearance Transparent or slightly turbid liquid Transparent or slightly turbid liquid

Density at temperature

(20+0,5) , g/m31,17 1,30 1,14 1,30

Alkalinity in terms of OH, % 13 -17 Not more than 17

Mass fraction of solids, % 25 35 23 33

Water-repellent ability Passed the test Passed the test

It is more preferable to use the GKZH -11K, not GKZH -11N, because when using the irst the salt elorescence on the surface is excluded.

Thoroughly clean the surface of dirt, laminated plaster, and remove a dust with an air (sweep of mechanically). If necessary, smooth the surface (cracks, cavities, bumps) with an appropriate mortar.

Prepare the solution in amount required for 12 hours of work, in the rate of 55 ml of water-repellent liquid GKZH-11K for 1 liter of water or 100 ml of water-repellent liquid GKZH-11N for 1 liter of water. If necessary, keep working solutions for a longer time (3 4 days) in a well-sealed glass or plastic container.

Apply a working composition on dry surface until the termination of absorption. Do not allow lowing and leaving drops. Do not work when raining, and after raining until the textured layer is dried. When uneven coating, received after treatment with GKZH-11K or porous surface, repeat the treatment, but only on the wet surface.

Workattemperaturenotlower5.Theviolationofthistechnologyandapplicationofthe working solution, retreatment on a dry layer, the excess of the solution applied, can lead to white elorescence on the treated surface.

Apply the working solution with brush, roller or by spraying.

The consumption of the working solution depends on the porosity of the treated material and it averages 350 ml per 1 m2.

Introduce water-repellent liquids GKZH-11K and GKZH-11N into the solution with mixing water in amount of 0,1-0,2 % by weight of binder cement or lime.

Water-repellent liquids are non-toxic, ireproof, but it has alkaline properties. Work in rubber gloves, glasses, spray upwind, use the respirator.


TU U 24.6-33444644-008:2009, amendment 1.

Physical and mechanical parameters of liquid GKZH-11 K

Surface treatment


Coating

Application methods

Material consumption the lat surface

Volumetric treatment

Safety information

Working solution preparation

31

EMULSION SE-50/12(analogs Silres BS 1042, BS 5136, Penta-812 (Penta, Russia))

EMULSIONS

Water emulsion of oligo dimethyl hydroxide siloxane, designed for water-repellency treatment of various materials, including glass iber and mineral wool products treated with phenol-formaldehyde resin.

To make glass iber mats or mats of mineral wool water resistant, mix the emulsion SE-50/12 with a solution of phenol aldehyde resin and other additives. If necessary, besides achieving water repellency efect, to prevent the formation of ine dust in the production of glass iber mats or mats of mineral wool, use the emulsion SE-50/12 in combination with ME-50/42. Mixing ratio is 1 part by weight of emulsion SE-50/12 for 3-5 parts by weight of emulsion ME-50/42. In this case, a mixture of emulsions also mixed with a solution of phenol aldehyde resin and other additives.

Since the shelf life of various mixtures mainly depends on the composition of phenol aldehyde resins and additives, it is impossible to give any general advice on their compatibility.

The emulsion SE-50/12 or the mix of emulsions SE-50/12 and ME-50/42 are used in combination with the binder.

The treatment of glass wool and mineral wool with the emulsion SE-50/12 or with the mix of emulsions SE-50/12 and ME-50/42 after drying and curing is not recommended.

Name of parameter Standard Regulated by

AppearanceHomogeneous liquid without

mechanical impurities. Color whiteGOST 20841.1 and

TU U 24.6-33444644-014:2010

Mass content of nonvolatile substances, %

at least 48 hoursGOST 17537 and

TU U 24.6-33444644-014:2010

Applications


Features

32


Funnel viscosity, at temperature (202,0)C,

30 - 150GOST 8420 and

TU U 24.6-33444644-014:2010

Stability on dilution, h at least 24 TU U 24.6-33444644-014:2010

Reaction of medium (pH 25% of water solution)

6,0 7,0 TU U 24.6-33444644-014:2010

Mass content of silicium, % 18 - 22GOST 20841.1 and

TU U 24.6-33444644-014:2010

Ignition point temperature, C Not presented GOST 12.1.044-89

Flash point temperature in closed cup, C

Not presented

Flash point temperature in opened cup, C

Not presented

The emulsion SE-50/12 or the mix of emulsions SE-50/12 and ME-50/42 is applied together with a binder by spraying method.

The amount of the emulsion SE-50/12 or of the mix of emulsions SE-50/12 and ME-50/42 depends on the required water-repellency properties of the inal product, so there is no general advice on how to use. The necessary amount can be determined after individual test. In most cases the introduction of at least 0,2% of the emulsion SE-50/12 or 0,6-1,2% of the mix of emulsions SE-50/12 and ME-50/42 from the weight of the dry ibrous material is enough.

TheshelflifeoftheemulsionSE-50/12 is 6 months from the date of manufacture. Store at temperature 5C to 30C in tightly closed containers of manufacturer in covered warehouses, protected from moisture, direct sunlight and away from heaters and tanks with strong oxidizing agents, alkalis and acids. Theusermaychoosetousetheproductaftertheexpirationofshelflifeperiod and the quality is checked to meet technical requirements of Water repellency emulsions.

The information on safety you can ind in safety data sheet, provided by our sales department on request.

Shelf life: 6 months. TU U 24.6-33444644-014:2010.

Water emulsion of mineral oil, intended for dust removal and optional water repellent treatment of various materials, including glass iber and mineral wool products treated with phenol-formaldehyde resin.

Topreventtheformationofinedustandmakewaterresistanttheglassibermatsor mats of mineral wool mix the emulsion ME-50/42 with a solution of phenol aldehyde resin and other additives. Since the shelf life of various mixtures depends on the composition of phenol aldehyde resins and additives, it is impossible to give any general advice on their compatibility. TheemulsionME-50/42 is used in combination with the binder ThetreatmentofglasswoolandmineralwoolwithemulsionME-50/42 after drying and curing is not recommended.

Features

Application:

EMULSION E-50/42EMULSIONS


Coating

Storage:

Safety information:

33

Application: To enhance the water-repellency efect use mixed with the emulsion SE-50/12.


AppearanceHomogeneous liquid without me-

chanical impurities. Color not speciiedGOST 20841.1 and

TU U 24.6-33444644-014:2010

Mass content of nonvolatile substances, %

at least 48 hoursGOST 17537 and

TU U 24.6-33444644-014:2010

Funnel viscosity, at

temperature (202,0)C, 30 - 150

GOST 8420 and

TU U 24.6-33444644-014:2010

Stability on dilution, h, at least at least 24 TU U 24.6-33444644-014:2010

not presented GOST 12.1.044-89

not presented GOST 12.1.044-89

>288 GOST 12.1.044-89

The emulsion ME-50/42 is applied together with a binder by spraying method. The amount of the emulsion ME-50/42 depends on the required water-repellency prop-erties of the inal product, so there is no general advice on how to use. The necessary amount can be determined after individual test. In most cases the introduction of 0,6 -1,2% of the emulsion from the weight of the dry ibrous material is enough.

The shelf life of the emulsion ME-50/42 is 6 months from the date of manufacture. Store at temperature 5C to 40C in tightly closed containers of manufacturer in covered warehouses, protected from moisture, direct sunlight and away from heaters and tanks with strong oxidizing agents, alkalis and acids. The user may choose to use the product after the expiration of shelf life period and the quality is checked to meet technical requirements of Water repellency emulsions.

The information on safety you can ind in safety data sheet, provided by our sales department on request.


Water emulsion of oligo dimethyl hydroxy siloxane and mineral oil.

For dust removal and additional water-repellent treatment of various materials, includ-ing iberglass and mineral wool products, processed with phenol-formaldehyde resin.


AppearanceHomogeneous liquid without mechanical

impurities. Color not speciied

Mass content of nonvolatile substances, %, at least 48

Funnel viscosity, 30 150

Stability on dilution, h, at least 24

Features

Application

EMULSIONSEMULSION SE-50/43(analog Pentamiks-843 (Penta, Russia))



Coating

Storage

Safety information

34

Topreventtheformationofinedustandmakewaterresistanttheglassibermats or mats of mineral wool mix the emulsion MSE-50/43 with a solution of phenol aldehyde resin and other additives. Since the shelf life of various mixtures depends on the composition of phenol aldehyde resins and additives, it is impossible to give any general advice on their compatibility. TheemulsionMSE-50/43 is used in combination with the binder ThetreatmentofglasswoolandmineralwoolwithemulsionMSE-50/43 after drying and curing is not recommended.

The emulsion MSE-50/43 is applied together with a binder.

Spraying.

The amount of the emulsion MSE-50/43 depends on the required water-repellency properties of the inal product, so there is no general advice on how to use. The neces-sary amount can be determined after individual test. In most cases the introduction of 0,6 1,2% of the emulsion from the weight of the dry ibrous material is enough.

The agent is non-toxic, ire and explosion proof, has little irritating action.


Water emulsions of polymethylsiloxane liquid of various concentrations. Depending on the mass content of liquid polymethylsiloxane we produce three types of emulsion KE 10-01:

Emulsion EC 10-01 (70%) - 70% concentration emulsion; Emulsion EC 10-01 (50%) - 50% concentration emulsion; Emulsion EC 10-01 (30%) - 30% emulsion concentration.

Emulsions are used as release agents for molds in tire and rubber industry, in the manufacture of rubber and plastic. In the foundry emulsions are used as release agents in the manufacture of rods based on furan resins for hot snap.

Name of parameter,

measuring unit

Standard for type

E 10-01 (70 %) E 10-01 (50 %) E 10-01 (30 %)

Appearance Homogenous liquid of white color

Content of mechanical impurities Not presented

Mass content of silicium, %, within 25,0 28,0 17,5-20,0 10,5-12,0

of water extract, within 6,0-7,5 6,0-7,5 6,0-7,5

Stability on dilution, hours, at least 24 24 24

Technological procedures in force on customers factory.

Theemulsionisnon-toxic,notlammable.Thereisnoirritationtoskinatshortterm contact usually. Remove in mechanical way with a cloth or paper. Rinse with a plenty of water or water with soap.

Features

EMULSION KE10-01(analog 3952)

EMULSIONS

Application:

Application:

Use regulated by

Safety information


Coating

Application method

Material consumption

Safety information

35

Aftercontactwitheyesthereisnoneedinmedicalcareusually. Theinformationonsafetyyoucanindinsafetydatasheet,providedbyoursales department on request.

Shelf life: 12 months. Store at temperature from 5 to 30. TU U 24.6-33444644-009:2009.

Water emulsion of oligo methyl hydride siloxane

forwaterprooingthesurfaceofconcrete,brick,asbestoscementandceramics, gypsum and other mineral surfaces; asawater-repellentadditiveinrepairingresidential,publicandindustrialbuildings and structures.

The surface of construction materials treated with liquid do not absorb moisture and is not destroyed by the cycles of freezing and thawing of water, which increases the life of the material.

Water-repellent coating does not change the appearance of the material, does not prevent the normal air ventilation within the construction, reduces dirt retention, and prevents the reduction of heat-insulating properties of the material, resistant to sunlight. The treated surface is not exposed to the damaging efects of mosses and lichens.


Appearance Emulsion of white to light gray color

Water-repelling ability, h At least 3,0

The ability to be diluted with water passed the test

Densityattemperature(25+0,5),g/cm3 0,980-1,020

Mass content of nonvolatile substanses, at least, % 50

Remove dust, dirt, grease, laitance and other contamination by any mechanical way.

Dilute the liquid with water in the ratio 1 part by weight of emulsion GKE 60-94 for 10 parts by weight of water. Thoroughly mix.

Apply a working composition on dry surface until the termination of absorption. Do not allow lowing and leaving drops. Do not work when raining, and outside temperaturelowerthan5.

Ceiling brush, roller, spraying.

Consumption of the working composition 350-500 g/m2.

Physiologically harmless.

Shelf life: 12 months. TU U 24.6-33444644-007:2009, amendment 1.

Features

Application

Coating


Consumption

Safety information



Preparation of the working composition

Surface preparation prior to water-repellency

treatment

Safety information

EMULSIONSEMULSION GKE 50-94(analogs Silres BS46; TP 3207)

36

The treatment of building constructions with water repellent can be provided in two ways:

1. Volumetric treatment, i.. in the preparation of concrete, cement or plaster solutions (as an additive 1.5% by weight of the binder - cement or lime), that reduces their water absorption and permeability, increases the plasticity of solutions, the strength of plaster and screed, increases frost resistance of the concretes of normal hardening regardless of their composition and the type of binder.

Introduce the emulsion with mixing water or into already prepared composition if mixed at least 20 minutes.

The studies found that the optimal concentration (commercial product) of GKE 50-94M in concrete / cement solutions is 1.5% by weight of cement. This amount of emulsion allows a minimal water absorption and permeability of solutions.The tests on the concrete F 200300 W 6 - 15 with water-repellent emulsion GKE 50-94 proved that it is required to use 5,25 kg of emulsion GKE 50-94 for production of the sample volume 1 m3.

2. Surface treatment - as a coating for protection of masonry, wallboard, cement and concrete ties, limestone, porous rock, slate, tile, plaster products.

For surface treatment, add one part of water emulsion GKE 50-94M to ten parts of water, stir and cover the surface with obtained composition until the stop of absorption, preventing drips and leaving drops. Apply the composition with a brush or paint sprayer. Repeat the treatment after drying (in 1-2 days).

The consumption of the working solution depends on the porosity of the material and it averages 350 ml per 1 m2.

When the surface treatment protect the surface from mechanical damage, when the bulk treatment the emulsion GKE 50-94 is distributed throughout the entire thickness of building material, resulting that mechanical damage to the upper layers do not afect the water-repellency of the lower layers.

INSTRUCTION FOR APPLICATION OF WATER-REPELLENT EMULSION GKE 50-94

EMULSIONS

37

ETHYLSILICATE 40

ETHYLSILICATES

Liquid is a mixture of tetra ethoxy silane and polyethoxy siloxanes.

Inthesteelindustryforprecisioncastingasacomponentofpartingpaintsandasabinder for the production of rods exposed to high temperatures. Inthetextileindustry for shrink-proof inish of wool cloth, to reduce shrinkage of rugs and make them resistant to dust and decay, as the impregnation of ilter fabrics. Inconstruction for the manufacture of water proof building materials, treatment of painted surfaces, impregnation of concrete to reduce the porosity, to receive silicosilicate and acid-resistant cement. In theglassandceramics industry for the enlightenment of optical glass, for the application of the light-scattering layer on the cylinders bulbs. It is used as a binding agent for the manufacture of ceramic materials that are resistant to the highly corrosive environments and have the mechanical strength, heat resistance and high dielectric properties, for the manufacture of highly resistant materials withstanding the temperature up to 1750C and a load of above 127kg/sm3. Inthepaintindustryasadditivesusedinformingoffast-drying,thermo-andwaterproofilm with resistant gloss. Physical and chemical properties.


Optical density at a wavelength of 400 nm, no more 1,4

Optical density at a wavelength of 670 nm, no more 0,3

Mass content of hydrogen chloride, %, no more 0,1

Mass content of ethyl alcohol, %, no more 1,5

Mass content of tetra ethoxy silane, % 10 - 15

Mass content of silicon dioxide, % 38 - 42

Densityat20,g/cm3 1,04 - 1,07

Applications:


Features

38


Duration of gelation, minutes 180 - 280

Freezing point temperature Lowerthan60

learfromcolorlesstoyellowish-broun.

Slight odor of ether.


Low toxic, explosive and ire-hazardous product.

Shelf life: 12 months. GOST 26371-84.


Color

Odor

Use regulated by

Safety information

Product of the partial hydrolysis and polycondensation of polyesters of orthosilicic acid.

In the foundry industry in the manufacture of ceramic molds for precise casting. In the manufacture of organic polymers as modifying additives conferring special properties. In the paint industry as a component of heat-resistant insulating enamels and paints, as well as matting additives for furniture varnishes.


Appearance Transparent or opalescent liquid

Mass content of hydrogen chloride, %, no more 0,07

Kinematicviscosity(20+0,5)C, 2,2-3,6

Duration of gelation, minutes, no more 30

Densityattemperature(20+0,5),g/m3 0,895-0,920

Mass fraction of silicium dioxide, % 17,0 21,0


The product is lammable. When operation, follow the rules of ire safety. It is recommended to use appropriate protective clothing, gloves and goggles or face protection. In case of contact with skin or eyes, rinse with a plenty of water and seek medical advice.


Store at temperature from -60 to 30.

TU U 24.1-33444644-011:2010 amendment 1.

Features

Application:

Use regulated by

Safety information


BINDER KP-1(analogs Silres BS OH 100, GC-20 P (Penta, Russia))

ETHYLSILICATES

39

A product of hydrolysis and polycondensation of polyesters orthosilicic acid.

The treatment of stone, concrete, brick, tile, plastered surfaces, gypsum products and other porous materials. Applied for treatment of new surfaces in order to preserve their attractive appearance, and during restoration work to restore the original strength.

Aquaprok-3 penetrates into the material and is polymerized, preventing the pen-etration of water, oil, grease and other contaminants, increases the strength, wear re-sistance and durability of the material. At the same time, treated materials keep their natural properties retain vapor permeability, i.e. can breathe. These properties are maintained for a long time.

After treatment the color of the stone becomes deeper and more saturated, showing the stone structure, which becomes more lively and enlightened creating the efect of wet stone.


Appearance Transparent or opalescent liquid

Mass content of hydrogen chloride, % no more 0,07

Duration of gelation, minutes, no more 30

Densityattemperature(20,0+0,5),g/m3 0,895 - 0,920

Depending on order, Aquaprok-3 is made with a glossy or matte efect.

The water repellent agent Aquaprok-3 is used for the treatment of a perfectly dry and clean stone. Moisture, dirt or dust can afect the result, in particular the uniformity of the treated surface. Use as much liquid as the stone can absorb under normal conditions. Treatindryweather,whenthetemperatureoftreatedsurfaceisintherangeof5Cto30C.Donotperformworkduringtherain,waitthetexturelayerisdried.Protecttreatedsurface from precipitation until water repellent agent is dried (about 24 hours at 20C).

Apply on dry surface until the termination of absorption. Do not allow lowing and leaving drops.

Wall brush, roller or spraying.

The consumption of the agent depends on the porosity of the treated material and it averages 0,12 l per 1 m2 of natural stone.

The agent is non-toxic. Observe ire safety rules when working. It is recommended to use protective cloth, gloves and glasses or face protection means. In case of contact with skin or eyes rinse with a plenty of water and seek medical care.

Shelf life: 3 months. Store at temperature from 40C to 30C.

TU U 24.1-33444644-011:2010 amendment 1.

Features

Application



Application

Coating

Safety information

Application methods

Material consumption the lat surface

WATER-REPELLENT AGENT FOR DECORATIVE

PURPOSE AQUAPROK-3ETHYLSILICATES

40

RESIN ED-16(analog of Lapox B-7)

EPOXY PRODUCTS

Features

Applications



Diane-epoxy resin (uncured).

It is used in electrotechnical, radioelectronic industries, air-, ship- and machine building, in building industry as a component of illing and treating compounds, glues, sealers, adhesives for reinforced plastics.

Parameter Standard

Premium grade First grade

AppearanceHighly adherent clear without visible mechanical

impurities and water

Color, iron-cobalt scale, not more than 6 10

Content of epoxy groups, % 16,0 18,0 16,0 18,0

Content of chloride ion, % not more than 0,002 0,005

Content of saponiiable chloride, %, not

more than0,4 0,6

Content of hydroxyl groups, %, not more than 2,5

Content of volatiles, %, not more than 0,2 0,6

Dynamic viscosity, P*s at 50C 5 18 5 20

Gelling time with hardener, h, not less than 4,0 3,0

People who working with epoxy resin ED-16 must be provided with workwear and individual security measures. All activities while working with epoxy resins must be realized in the premises, equipped with lowing-exhaust ventilation.

Epoxy-diane resin ED-16 is stored in tightly closed tare in closed warehouses at temperature not higher than 40. Shelf time of epoxy resin ED-16 is 12 months

from manufacturing date. DSTU 2093-92.

41

Diane-epoxy resin (uncured).

It is used in electrotechnical, radioelectronic industries, air-, ship- and machine building, in building industry as a component of illing and treating compounds, glues, sealers, adhesives for reinforced plastics.

Parameter Standard

Premium grade First grade

AppearanceHighly adherent clear without visible mechanical

impurities and water

Color, iron-cobalt scale, not more than 4 12

Content of epoxy groups, % 19,9 22,0 19,9 22,0


Content of saponiiable chloride, %, not

more than0,5 0,9

Content of hydroxyl groups, %, not more than 1,7

Content of volatiles, %, not more than 0,5 0.90.5

Dynamic viscosity, P*s at 50C 2 18 12 25

Gelling time with hardener, h, not less than 5,0 4,0

People who working with epoxy resin ED-20 must be provided with workwear and individual security measures. All activities while working with epoxy resins must be realized in the premises, equipped with lowing-exhaust ventilation.

Guaranteed shelf life: Epoxy-diane resin ED-20 is stored in tightly closed tare in closed warehouses at temperature not higher than 40.

Shelf time of epoxy resin ED-20 is 18 months from manufacturing date.

DSTU 2093-92.

Epoxy resin E-40 (uncured).

It is used for manufacturing enamels, varnishes, illings, and also as semi-inished product for manufacturing other epoxy resins, illing mass, and glues.

Parameter Standard

Premium Standard

AppearanceHighly adherent clear without visible

mechanical impurities and water

Color, ISHM, mg I 2 /100 cm2, not more than 3 5

Purity of resin solution, %, light releasing, not less than 73 73

Content of non-volatiles, %, not less than 94 94

Features

Features

Application

Application




RESIN ED-20(analog of Lapox B-13, resin 0164, the resin CYD 128)

RESIN E-40

EPOXY PRODUCTS

EPOXY PRODUCTS

42

Parameter Standard

Relative viscosity of resin solution, viscometer

-246(3-4) with nozzle diameter 4 mm at

(20.00.5), s solution 2:1 in toluene25 40 25 40

Content of epoxy groups, % 13 15 13 15


Content of saponiiable chloride, %, not more than 0,30 0,35

People who working with epoxy resin E-40 must be provided with workwear and individual security measures. All activities while working with epoxy resins must be realized in the premises, equipped with lowing-exhaust ventilation.

Guaranteed shelf life: epoxy-diane resin E-40 is stored in tightly closed tare in closed warehouses at temperature not higher than 40. Shelf time of epoxy resin E-40 is 18 months from manufacturing date.TU 2225-154-05011907-97.




Two-component paint material comprising base enamel (suspension of pigments, plasticizers, illers in the solution of epoxy and urea-formaldehyde resins with the addition of dispersants) and hardener.

To form radiation-resistant, decontaminated surfaces of concrete and metal surfaces, structures, interiors and exterior surfaces of equipment of nuclear power, including in the area of high security.


Appearance of coatingCoating smooth, uniform, glossy,

without foreign impurities

Funnel viscosity of enamel basis, , at least 70

Mass fraction of solids in the basis of the enamel, %, at least 52

Milling degree of enamel basis, um, no more 35

Dryingtimetodegree3attemperature(202),h,nomore 20

Bending elasticity of the coating, mm, no more 1

Coating impact strength, on the device U-1a m, at least 40

Coating adhesion, points, no more 1

Viabilityofenamelat(202),h,atleast 7

Spreading rate of enamel, g/m2, no more 140

Wide color range is available. It is possible to select colors by RAL or costumer sample.

Remove dust, dirt, oil, iron oxides, rust and other contamination by any mechanical means (the best way to prepare metal surfaces for painting is sandblasting), degrease with organic solvents.

thoroughly mix and ilter base of enamel EP-5; 30 minutes before applying introduce the amine hardener in a ratio of 5 parts by

Features

Application

Colour


Enamel preparation:

ENAMEL EP-5 KEPOXY PRODUCTS

43

Enamel preparation:

Coating



Safety information:

weight of hardener for 100 parts by weight of base, or as indicated in the passport; thoroughly mix and dilute if necessary to the desired viscosity with solvents R-4, R-5; use enamel within 7 hours since the moment of preparation.

Apply enamel in 2-3 layers on surfaces, coated with iller EP-0010 before. Apply subsequent layers of enamel with an interval of 24 hours (till complete drying) after application of each layer.

with brush, roller (relative viscosity of enamel 55-80 ); pneumatic spraying (relative viscosity of enamel 25-30 ); airless spraying (relative viscosity of enamel 30-55 ).

Material consumption per one layer on a lat surface primed: hand method from 160 g/m2; pneumatic spraying from 200 g/m2 ; airless spraying from 190 g/m2 ;

The enamel ilm in cured state is not toxic and ireproof.


TU U 24.3-33444644-004:2006 amendment 1.

Two-component paint material comprising base enamel (suspension of pigments, ill-ers in a solution of epoxy resin in a mixture of organic solvents) and amine hardener.

It is used for coloring previously primed metal and non-metal surfaces to create limited weatherproof coatings, operating in areas with moderately cold climate and humid conditions, the actions of the sea water, and its vapors, and special environments. Dark gray graphite enamel is used for conductive coatings when applied to products from silicone iberglass. It is also used on nuclear facilities.


Appearance of coatingMatte or semi-matte inish, homogene-

ous, without foreign impurities



Milling degree basis enamel, um, no more

Dark-green

Dark-red,dark-gray-graphitizedRest of colours

45

Not deined

40

Drying time, h, no more:

Todegree5attemperature(505)Todegree3attemperature(1205)

5

2

Features

Application

ENAMEL EP-525 K EPOXY PRODUCTS


44


Film hardness by pendulum TML (pendulum ), conventional relative units, at least

0,30

Bending elasticity of the coating, mm, no more 2

Coating impact strength, on the device U-1a m, at least 40

Coating adhesion, points, no more 1

Viabilityofenamelat(202),h,atleast 8

Spreading rate of enamel, g/m2, no more 170

Volumeresistivityofcoating,Ohmcm,nomore(forenameldark-gray graphitized)

10

Wide color range is available. It is possible to select colors by RAL or consumer sample.

Remove dust, dirt, oil, iron oxides, rust and other contamination by any mechanical means (the best way to prepare metal surfaces for painting is sandblasting), degrease with organic solvents.

thoroughly mix and ilter base of enamel EP-525K; 30 minutes before applying introduce the amine hardener in a ratio of 3 parts by weight of hardener for 100 parts by weight of base, or as indicated in the passport; thoroughly mix and dilute if necessary to the desired viscosity with solvents R-5, R-5A; use enamel within 8 hours since the moment of preparation.

applyenamelin2-3layersonsurfaces,coatedwithprimerbefore.Applysubsequent layers of enamel with an interval of 24 hours (till complete drying) after application of each layer; asaprimerformetalsurfaces,usealayerofprimercoatingAK-070,EP-0020oriller EP-0010K, on concrete surfaces two layers of iller EP - 0010 or EP - 0020.

with brush, roller (relative viscosity of enamel 55-80 ); pneumatic spraying (relative viscosity of enamel - 25-30 ); airless spraying (relative viscosity of enamel 30-55 ).

Material consumption on a lat surface primed: one layer from 170 g/m2.

The enamel ilm in cured state is not toxic and ireproof.

Shelf life: 12 months. TU U 24.3-30552853-002-2002, amendment 1-4.


Colour


Enamel preparation:

Coating:



Safety information

Two-component paint material comprising base enamel (suspension of pigments, illers and functional additives in a solution of epoxy and urea-formaldehyde resins) and amine hardener.

For coloring concrete, metal surfaces, inishes of building structures, premises with ag-gressive media, the outer surfaces of industrial equipment, as well as decontaminated

Features

Application

ENAMEL EP-574 EPOXY PRODUCTS

45

inish of building structures, premises and external surfaces of equipment of nuclear power. The enamel forms decontaminated surface.

Name of parameter and unit of measure Norm

Appearance of coating Homogeneous smooth surface.



Milling degree basis enamel, um, no more 35

Dryingtimetodegree3attemperature(202),h,nomore 20

Film hardness by pendulum TML (pendulum ), conventional relative units, at least

1. «Korona-2000» Ltd. (Ukraine). 2. OJSC «SILAN»,...

Documents

Transcript of 1. «Korona-2000» Ltd. (Ukraine). 2. OJSC «SILAN»,...