NITROGEN STEEL All steels contain some nitrogen which is effective in improving
the mechanical and corrosion properties of steels if it remainsin solid solution or precipitates as very fine and coherentnitrides
When nitrogen is added to austenitic steels it can
simultaneously improve fatigue life, strength, work hardeningrate, wear and localized corrosion resistance.
High nitrogen martensitic stainless steels show improvedresistance to localized corrosion (pitting, crevice andintergranular corrosion) over their carbon containing
counterparts
However, solidification of steel may result in three nitrogen-related phenomena: formation of blowholes; precipitation ofone or more nitride compounds; and/or the solidification ofnitrogen in interstitial solid solution.
8/12/2019 mechanical behviour
3/11
EFFECT OF NITROGEN ON STEEL
PROPERTIES The effect of nitrogen on steel properties can be either
detrimental or beneficial, depending on the other alloyingelements present, the form and quantity of nitrogen present,and the required behavior of the particular steel product.
In general, however, most steel products require that nitrogenbe kept to a minimum. High nitrogen content may result ininconsistent mechanical properties in hot-rolled products,embrittlement of the heat affected zone (HAZ) of weldedsteels, and poor cold formability.
Hardness is the resistance of a material to surface indentation
8/12/2019 mechanical behviour
4/11
Nitrogen absorbed during steelmaking results in interstitialsolid solution strengthening and grain refinement, both ofwhich increase hardness.
further, the diagram shows that nitrogen absorbed during thesteelmaking process has a more significant impact than that
absorbed during batch annealing in a nitrogen-richatmosphere, although both have a measurable effect
8/12/2019 mechanical behviour
5/11
8/12/2019 mechanical behviour
6/11
Note that many intermetallic compounds areoften simply called 'alloys', although this issomewhat of a misnomer. Both are metallicphases containing more than one element, but
in alloys the various elements substituterandomly for one another in the crystalstructure, forming a solid solution with a rangeof possible compositions; in intermetallic
compounds, different elements are ordered intodifferent sites in the structure, with distinct localenvironments and often a well-defined, fixedstoichiometry. Complex structures with very
large unit cells can be formed.
8/12/2019 mechanical behviour
7/11
NICKEL ALUMINIDE
Nickel aluminide (Ni3Al) is an intermetallic alloy ofnickel and aluminum
The alloy is very resistant to heat and corrosion,
and finds use in heat-treating furnaces and other
applications where its longer lifespan and
reduced corrosion give it an advantage over
stainless steel.
Nickel aluminide is unique in that it has very high
thermal conductivity combined with high strength
at high temperature.
Used in coating blades of gas turbines and jet
engines.
8/12/2019 mechanical behviour
8/11
COMPOSITION AND
STRUCTURE Boron additions were critical for achieving the reasonable level
of ductility in the alloys
Boron is thought to increase grain boundary cohesiveness,thereby reducing the tendency for brittle intergranularstructure
The unit cell consists of FCC arrangement in which thealuminium atoms occupy the corner position, nickel atom
preferably occupy the face centred position This type of atom packing leads to mechanical properties
As the temperature increases, also the yield strength increases,
8/12/2019 mechanical behviour
9/11
CORROSION RESISTANCE
8/12/2019 mechanical behviour
10/11
CORROSION RESISTANCE
Oxidation and carburization resistance of nickelaluminide alloy are shown in above diagram
Nickel aluminide alloy form a protective Al2O3
scale on the surface have significantly better
oxidation resistance than aluminium free alloy
Carburization resistance also high under
oxidation
APPLICATIONSPistons and valves, automotive turbo charges,
aircraft fasteners,gas water and steam turbines
8/12/2019 mechanical behviour
11/11
TITANIUM ALUMINIDE
. It is lightweight and resistant to oxidation [1]andheat, however it suffers from low ductility.
Titanium aluminide has three major intermetallic
compounds: gamma TiAl, alpha 2-Ti3Al and TiAl3
TiAl based alloys have a strong potential to
increase the thrust-to-weight ratio in the aircraft
engine.