E4215Mechanical Behavior of Materials

Lecture 10 Dislocations and Slip ‐ II

Prof. K. Barmak

1

Outline

• Single crystals deformed in tension– Slip systems– Schmid factor– Critical resolved shear stress– Rules for identifying slip systems

• Peirls‐Nabarro stress• Dislocation motion  

– Glide, cross slip of screw dislocations– Climb

• Jogs and kinks

2

Slip Systems ‐ I

• 5 independent slip systems are needed for an arbitrary shape change

• Dislocations glide on planes of highest atomic density (i.e., on close‐packed planes) in close‐packed directions– fcc Al, Cu, Au, Ag, Ni– bcc  Fe, W, Nb

• Slip direction is in the slip plane, therefore, it is normal to the normal to the plane

3

{111} 110 {110},{112}or{123} 111

Slip Systems ‐ II• hcp: depends on the c/a ratio

• Basal slip if c/a >  ideal ratio 1.633: • Basal slip or prism slip if c/a <ideal ratio: 

4

{0001} 1120

{1010} 1120

More densely packed than basal plane when c/a < ideal ratio

Slip Systems in FCC Metals• Note that since {} and <> mean families of planes and directions, there are a number of distinct slip system for a given {hkl}<uvw>

• So for example for the face centered cubic crystal there are twelve distinct slip system

5

{111} 110 4 slip planes 3 slip directions in each plane

111

111

111

111

110 101 011

Note that the slip directions must be in the slip planes.  Therefore, the normal to the slip plane, here,  [hkl] must be normal to the slip direction [uww]. The dot product must be zero, i.e., must have hu+kv+lw=0.

e.g., in (111)

Dislocations in FCC Metals

• Relation between slip direction and Burgers vector– slip direction

– Burgers vector

6

1 1102

22

a

b

b

110

Vector joining the nearest neighbor atoms

a is the lattice parameter

Dislocations in BCC Metals – I • Close(st)‐packed planes: {110}• Close‐packed directions: <111>• Burgers vector: 

– b = a/2<111>– Magnitude of Burgers vector

• Glide occurs on {110} planes, in <111> directions• Each unit cell contains 6 {110} type planes (not counting the planes with the negative of all indices, e.g., count (110) but not (‐1 ‐1 0) )– Each {110} plane contains two <111> directions

• Therefore there are 12 {110}<111> type slips system 

7

3b2

a

Dislocations in BCC Metals ‐ II

• In BCC, slip can also occur on {112} and {123} planes in <111> directions

• Each unit cell contains 12 {112} planes– Each {112} plane contains 1<111> direction

• Thus there are 12 {112}<111> slip systems

• Each unit cell contains 24 {123} planes– Each {123} plane contains 1<111>

• Thus there are 24 {123}<111> slip systems

• Thus there are  total of 48 slip systems in BCC metals.

8

Dislocations in BCC Metals ‐ III

• Slip on {110} is most prevalent• Three {110} planes intersect a <111> direction, therefore, unit screw dislocation can easily move from one {110} to another {110} or to {123} and {112} planes, resulting in wavy slip lines.

• Extended dislocations are uncommon in BCC.

9

Dislocations in HCP Metals

• Relation between slip direction and Burgers vector– Close‐packed directions: – Burgers vector:– Magnitude of Burgers vector: a

10

11201120

3a

http://www.cmmp.ucl.ac.uk

Deformation of a Single Crystal in Tension

11

Normal to slip plane

Applied force

Applied force, F

Slip direction

Slip plane

FA

cos cosFA

(Engineering) stress is force per unit (initial) area:

Resolved shear stress

Slip occurs in a particular crystal direction on a particular slip when the resolved shear stress reaches a critical value, C .  Slip therefore occurs on the slip system with the highest Schmid factor.

Schmid factor

Area normal to the load, A

Normal stress in the oblique plane

2cosN

Example 1

• A face centered cubic single crystal is loaded in the [100] direction.  What is the Schmidfactor for the slip system given below?

12

[110](111)

0.408

Example 2

13

Critical Resolved Shear Stress

14

• The experimental evidence of Schmid’s Law is that there is a critical resolved shear stress.  This is verified by measuring the yield stress of single crystals as a function of orientation.  The example below is for Mg which is hexagonal and slips most readily on the basal plane (all other crss are much larger).

“Softorientation”,withslipplaneat45°totensileaxis

“Hardorientation”,withslipplaneat~90°totensileaxis

coscos

Simple Rules for Identifying Slip Systems 

15

OILS Rule

16

OILS Rule ‐ Example

17

Diehl’s Rule: FCC Crystals ‐ I

18

Diehl’s Rule: FCC Crystals ‐ II

19

Diehl’s Rule – BCC Crystals

20

Slip and Rotation of Crystal

• Before and after deformation • Note the rotation of crystal when using fixed grips

21

Dieter

Geometric Softening and Hardening

22

Conjugate Slip System ‐ I

23

Conjugate Slip System ‐ II

24

Conjugate Slip System ‐ III

25

Crystal Rotation During Plastic Flow

26

Slip Traces ‐ I

27

Slip Traces ‐ II

28

Slip Traces

• Slip traces are observed where dislocation glide planes intersect the polished face of a crystal– Therefore, a slip trace represents a direction comment to the two crystal planes

• In cubic crystals, the slip trace can be obtained via the cross product of the normals to these two planes

29

Before glide

After glide

Slip trace on crystal face

h1 k1 l1 h1 k1 l1h2 k2 l2 h2 k2 l2

1 2 1 2 1 2 1 2 1 2 1 2k l l k l h h l h k k h

Peirls‐Nabarro Stress ‐ I• The critical resolved shear stress needed to cause dislocation glide is the Peirls‐Nabarrostress (or Peirls stress) , which represents the inherent lattice resistance to the movement of dislocations

30

2 2exp1

1

p

edge

screw

G wb

dw

w d

Poisson’s ratio

Interplanar spacing

Burgers vector

Peirls Stress ‐ II

• c (or p) exists• Highest for covalent solids• Lower for metals• Decreases as width of the dislocation core increases

• Decreases with increasing temperature

31

Outline

• Single crystals deformed in tension– Slip systems– Schmid factor– Critical resolved shear stress– Rules for identifying slip systems

• Peirls‐Nabarro stress• Dislocation motion  

– Glide, cross slip of screw dislocations– Climb

• Jogs and kinks

32

Dislocation Motion

• Two types of dislocation motion– Glide: Dislocation moves in glide plane, i.e., the plane that contains both the dislocation line and the Burgers vector

– Climb: Dislocation moves out of glide plane normal to the Burgers vector

33

Dislocation Glide ‐ I

34

• Recall the effect of dislocation motion in a crystal: passage causes one half of the crystal to be displaced relative to the other.  This is a sheardisplacement, giving rise to a shear strain.

[Dieter]

Stress‐Strain Curve• Deformation at intermediate temperatures mediated by  dislocation glide:

35

Dislocation Glide ‐ II• Dislocation Glide under the application of a shear stress:

• Conservative motion (volume conserved)• Glide of many dislocations = slip

– Slip: two undeformed blocks of the crystal move relative to each other

36

Do not confuse how b was defined, with the direction in which the dislocation will move under an applied shear stress.

Dislocation Glide ‐ III• For edge dislocations, glide plane is uniquely defined since dislocation line and Burgers vector are perpendicular to each other

• Screw dislocations have their line and Burgers vector parallel, therefore, they can easily change their glide plane– This is known as cross slip

37

Plastic Shear Strain and Dislocation Glide

• Plastic shear strain associated with dislocation glide

38

tan mDshear strain b xh

Magnitude of Burgers vectorMobile dislocation density

Average distance moved by dislocation

Dislocation Climb• Climb is non‐conservative (volume not conserved)

– Vacancies and diffusion are required for climb, and, as a result higher temperatures are required for this type of motion

39

Plastic Strain and Dislocation Climb• Plastic deformation of crystalline materials at high temperatures is termed creep

40

Plastic  (engineering) strain parallel to b resulting from climb of edge dislocation

eng mh b x

h

Average distance climbed by a dislocation

h

h

d

Jogs and Kinks ‐ I• Jogs move the dislocation line from one plane to another plane– Jogs can form by dislocation climb since climb does not occur over the whole length of the line; it occurs only on certain segments of the line, resulting in the formation of jogs

– Jogs can also form by intersection with other dislocations

41

Jogs and Kinks ‐ II• The jog should be contrasted with kinks, which displace the dislocation line on the same plane

42

Jogs and Kinks ‐ III• The jog and kink on an edge dislocation 

43

Jogs and Kinks ‐ IV• Jogs and kinks have the same b as the rest of the dislocation• Kinks do not impede dislocation motion, because they are on the same 

slip plane• Jog on edge does not impede dislocation glide• Jog on screw does impede glide because has edge character, and requires 

climb for motion

44

Shear stress