2.1. Barium Titanate (BT):
One of the most versatile compounds in the field of ceramic science and
engineering is BaTiO3, (BT) which belongs to ABO3 family. It has typical crystal
structure and illustrates phase transition with change in temperature. Researchers are
making many attempts to study BT compound by synthesizing it by various well-known
and modified procedures to get a BT in various forms such as single crystal, thin film,
etc.
Another powerful technique is to perform substitution studies at cationic sites of
BT ceramics. Doping can be done at one site or at both the sites by iso-valent and or alio-
valent ions, individually or simultaneously. This practice is to explore the novel
applications of BT.
The extensive research work done on BT compounds are mentioned below:
Before 1940, only two types of ferroelectrics were known, Rochelle salt and
potassium dihydrogen phosphate and its isomorphs [1]. In the early 1940’s, the discovery
of BT ceramics, the first ferroelectric ceramic without hydrogen bonds, has led to the
discovery of a large number of similar type of perovskite ceramics viz. KNbO3, LiNbO3,
PT etc. [2].
Polycrystalline ceramics have advantage over single crystals, because
polycrystalline ceramics can be formed into any desired shape, the orientation of polar
axis can be chosen and synthesis process is cheaper than the single crystal growth
process. The major breakthrough in the research on ferroelectric materials came in the
early 1950’s with the widespread use of BT based ceramics in capacitor applications and
piezoelectric transducer devices [3].
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 26
After 1950, many other ferroelectric ceramics including lead titanate (PT), lead
zirconate titanate (PZT), lead lanthanum zirconate titanate (PLZT) etc. (particularly lead
oxide based) have been developed, which find their use in various applications and
devices. These lead oxide based systems are the most widely used materials for
piezoelectric transducers, actuators and transformers due to their excellent piezoelectric
properties close to the morphotropic phase boundary (MPB) compositions [4].
H. Diamond et al (1961) studied the variation of ε with E in perovskite-like
ferroelectrics. It was reported that the variation of incremental ε is associated with an
induced ferroelectric state rather than being directly a property of domain processes, and
that a large variation with E must necessarily be accompanied by strong thermal
sensitivity [5].
K. M. Johnson et al (1962) reported the variation of ε with voltage in
ferroelectrics and its application to parametric devices, functional relationship between ε
and voltage for a ferroelectric in the paraelectric state was derived, and Fourier
capacitance coefficients for different applied voltage functions were computed. It was
showed that because the Tan δ of a ferroelectric in the paraelectric state is proportional to
frequency, it can be represented in the same way as a varactor [6].
K. Uchino et al (1989) shows that there is a relationship between the particle size
and the c/a ratio for ferroelectric materials. Smaller particle sizes leads to a c/a ratio close
to 1.00(c/a=1.00 implies a cubic structure) [7].
K. Uchino et al (1989) investigated the effect of the sample particle size on the
crystal structure and the Tc of BT powder in the particle size range 0.1 to 1.0μm and
reported that the transformation from tetragonal to cubic symmetry occurs at a critical
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 27
particle size of 0.12μm at room temperature, the Tc drops below room temperature at the
critical particle size [8].
A.I. Kingon et al (1996) reported that the high r perovskite for the application of
ferroelectric films is their incorporation into DRAMs as the storage node capacitor
dielectric. DRAMs represent a large market that is experiencing strong growth, but they
were particularly significant as the technology leader for semiconductor devices [9].
H.Takasu (2000) discussed the ferroelectric memory was not only an ideal
memory with clear advantages such as non-volatility, low power consumption, high
endurance and high speed writing, but is also the most suitable device for memory
embedded applications. The ferroelectric memory based reconfigurable devices can be
used as Dynamic Programmable Gate Array (DPGA), which were able to be reconfigured
from their original logic in a system under an operation mode [10].
S.B.Park et al.(2000) prepared of Pb(Yb1/2Ta1/2)O3-PT by the solid solution, the
crystal structure and the dielectric properties were investigated in terms of the PT
concentration. As the PT concentration increases, the crystal structure changes from
monoclinic to pseudocubic to tetragonal [11].
E. Tuncer et al (2002) reviewed the current state of understand of dielectric
mixture properties, and approaches to use numerical calculations for their modeling are
presented. It is shown that interfacial polarization can yield different non-Debye
dielectric responses depending on the properties of the constituents, their concentrations
and geometrical arrangements and discussed the future challenges on dielectric mixtures
[12].
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 28
Christos D. et al (2002) reviewed the Organic thin-film transistors (OTFTs)
conduction mechanisms and performance characteristics, as well as opportunities for
modeling properties of OTFTs. The shifted focus in research from novel chemical
structures to fabrication technologies that optimize morphology and structural order is
underscored by chapters on vacuum-deposited and solution-processed organic
semiconducting films and discussed in the growing field of the n-type OTFTs [13].
K.F. Astafiev et al (2003) investigated the influence of addition of a low-loss
linear dielectric material to a tunable ferroelectric material in terms of the electrostatic
consideration. The calculations of the Tan δ and dielectric non-linearity of ferroelectric-
dielectric composites have been performed by using three different models. On the basis
of results obtained, the figure of merit of the composite material has been evaluated. No
improvement of the figure of merit of composite material compared to the pure
ferroelectric has been observed for the considered models [14].
A. K. Tagantsev et al (2003) reviewed the properties of ferroelectric materials that
are relevant to µw tunable devices and discussed the theory of dielectric response of
tunable materials and presented the techniques for characterization of tunable
ferroelectrics and applications of these materials [15].
V.Buscaglia et al. (2004) reported the preparation and the properties of BT
ceramics and thick films .The ceramics were prepared by spark plasma sintering at 800˚C
of nanopowders produced by a wet chemical process, while films were fabricated by air
flow deposition of mixed fine and coarse powders at room temperature followed by
isothermal firing. The transition from ferroelectric to paraelectric state was broadened
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 29
over a wide range of temperature with Curie–Weiss parameters strongly depressed in
comparison to grained ceramics [16].
M. Cernea (2005) synthesized the BT powder of particle size range 80nm,
calcined at 950°C, X-ray analyses indicates that the material exhibits a tetragonal, poorly
crystallized. The powder pressed and sintered at 1275°C show high , i.e. 1300 at 25°C
and, 3020 at the Tc (104°C). The melting point for BT prepared by sol-gel technique is
1290°C [17].
C.Pithan et al. (2005) studied the progress in the synthesis of nanocrystalline BT
powders for using highly volume efficient MLCC from the synthesis approach of both
liquid and solid precursors that is oxalate or citrate route. The technically and industrially
most relevant technique for the synthesis of nano sized BT powders, for practical
application was also highlighted [18].
A Sreenivasalu et al (2007) reported that the optimization of the sintering
temperatures of dielectric material such as BT and LiNbO3 in the form of pellet ceramics.
The optimized temperature for BT is 9500C and in LiNbO3 it is 900
0C based on the
temperature optimization studied carried out in the temperature range 800-10000C. The
crystallanity nature has symmetrically been analyzed through the XRD and FTIR spectral
measurements. Crystallization nature of the materials has been found to be tetragonal
based on the XRD. Such tetragonal crystalline natured dielectric materials are of
technological importance and significant relevance in the progress of wide variety of
opto-electronic materials [19].
F.F.Hammad et al.(2008) studied the XRD study on structural characteristics of
pure and doped perovskite BT. They reported that transformation from tetragonal to
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 30
cubic system and values of tetragonality (c/a = 1.0084-1.0095) are in agreement with that
of the pure BT of perovskite structure. Gd is not recommended as additive to get single
phase BT [20].
W.Li et al. (2009) studied the structure and electrical properties of BT prepared
by sol-gel process. The results indicated that both the grain size and the relative density
of the ceramics increased with the increase in sintered temperature. The at the room
temperature was not sensitive to the grain size [21].
E.E.Oren et al.(1999) reported the preparation of mono size and crystalline BT
by using hydrothermal synthesis. This process commonly uses the starting materials of
water-soluble inorganic Ba(OH)2·8H2O salt and insoluble TiO2 powders, to be mixed an
aqueous solution kept at room temperature near its boiling point for prolonged times.
Hydrothermal synthesis involves the formation of crystalline materials from the starting
materials in such aqueous media, under strongly alkaline conditions. Hydrothermal
processing of BT powders has always required the use of a certain quantity of excess
barium hydroxide in the starting mixture to speed up the hydrothermal reactions. Showed
that successful preparation of BT by hydrothermal processing required a pH>12 in
aqueous solution kept near the boiling point. They also underlined the importance of
eliminating CO2 from the reaction vessel to avoid the formation of BaCO3 [22].
C.Pithan et al. (2006) reported comprehensive review of preparation, processing
and characterization of BT powders and ceramics derived from micro-emulsion mediated
synthesis [23].
Y.Mao et al. (2010) prepared BT nanoparticles with various particle sizes by a
solvothermal method. SEM reveals that all the particles of BT with different size are
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 31
dispersed homogeneously and have uniform size. The effects of the reaction parameters,
such as the concentration of reactant, the polarity of solvent, the reaction temperature
and the amount of surfactant, on the size, morphology and uniformity of BT
nanoparticles are studied [24].
2.2. Modification of ABO3:
Viswanath et al (1997) studied the nature of the ferro-paraelectric transition
(FPT) of BT depends on its crystallite size. The ε values were determined from the
complex-impedance plot in the frequency range between 100Hz and 107Hz at various
temperatures and reported that the ε values obtained at the transition region (around
120°C) are very low and the spectra obtained are quite broad. Ferroelectricity vanishes on
doping BT with different valence state elements (Sn, Zr, Bi, Sb, Fe, Zn, Cu and Pb) in
92:8 mol. ratios [25].
P.K.Panda (2009) reviewed on the developments in environment friendly
piezoelectric materials was done by Symptoms and signs of lead Lead (Pb) poisoning
properties of some selected Pb-free compositions, for example, BT, Bi0.5Na0.5TiO3,
(Na0.5Bi0.5)0.92 Ba0.08TiO3, (Na0.5Bi0.5)0.92 Ba0.08TiO3+xNb2O5 etc. Effects of dopants on
their various properties along with phase relation between the individual components
involved in the formation of solid state solution of perovskite structure materials [26].
Ching-Fang Tseng et al (2009) discussed a new ultra low Tan δ μw dielectric
ceramic, Mg(Sn0.05Ti0.95)O3(MSnT). The compounds were prepared by the conventional
solid-state route, and sintered at 1360°–1480°C for 2–6h. The investigations show that
the MgTi2O5 secondary phase was observed. Moreover, dielectric properties were
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 32
correlated with the formation of second phase. The excellent μw dielectric properties
were obtained from the new MSnT ceramics sintered at 1390°C for 4h [27].
Takashi Teranishi et al (2010) analysed the polarization behavior in relaxation of
BT-based ferroelectrics using wideband dielectric spectroscopy in dielectric spectra from
the kilohertz to terahertz range. Ceramics of BT, BST, and BZT were selected as normal
ferroelectrics, DPT ferroelectrics, and relaxor ferroelectrics, respectively. The variation
of ionic polarization in both BT and BST ceramics with temperature are explained by the
softening of the soft phonon mode. In BZT, found ε anomaly at the ε maximum
temperature (Tm) at low frequencies is not attributed to the softening of the soft phonon
mode, but originates from the ε derived from the dipole polarization. Relaxor behavior in
BZT is derived from the increase in the depression of ε dipole on cooling across the Tm
with increasing frequency. In dipole polarization, BT, BST, and BZT all exhibited a
similar tendency of ε dipole above the Tc and Tm. However, behavior of ε dipole below
the Tc can be explained by the ferroelectric domains in BT, whereas the variation of ε
dipole below the Tm could be explained by growth process of polar nano-regions [28].
2.3. A-site modification of ABO3:
I.M.Reaney et al. (1994) studied the dielectric and structural characteristics of Ba-
and Sr-based complex perovskite as a function of temperature. Tolerance factor
influences the structure and the value coefficient of the ε studied [30].
A.I. Kingon et al. (1996) investigated the temperature dependent dielectric
behavior of BST [29].
L.C.Sengupta et al. (1999) reported that the BST combined with other non-
electrically active oxide ceramics was useful for low Tan δ, tunable dielectric materials
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 33
which are important for phased array antenna and other device applications. The ε , Tan δ
of these composites have been reduced to enhance the overall impedance matching and
thereby lowering the overall insertion loss of the device and discussed the material
fabrication methods and the electronic properties of these composites [30].
P.H.Chen et al. (2000) estimated the microstructural characteristics and non-
equilibrium core-shell phase in (PbxSr1-x) TiO3 materials and their electrical properties
shows that the specimens prepared by μw sintering exhibited a single Tc, whereas those
prepared by conventional sintering show a double Tc behavior [31].
S. Ezhilavan et al. (2000) reviewed the developments, deposition techniques,
post-annealing, physical, electrical, dielectric characteristics and the effects of electrode
materials, dielectric relaxation and defect analysis and the reliability phenomena
associated with the BST thin films for future Giga bit era DRAM applications [32].
R.Wang et al. (2001) studied the dielectric properties of BST solid solution. The
ε, pyroelectric measurements have confirmed the quantum paraelectric to the quantum
ferroelectric phase transition in solid solution with [33].
B.D.Stojanovie et al. (2001) have studied the structural and electrical
characteristics of semiconducting BPT ceramics. In this they investigated that the
addition of 5 mol% of Al2O3, SiO2 and TiO2 as additives to the Sb2O3 MnSO4 and ZnO
doped BPT system controlled the abnormal grain growth of this system [34].
D.Shiwen et al. (2001) hypothesized theoretically that the Tc of BT may be
lowered and broadened when either the large Ba2+
ions are partially replaced by small-
sized Sr2+
or Zn2+
, or the active Ti4+
ions are partially replaced by non-active Zr4+
or
Sn4+
[35].
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 34
K.Park et al. (2002) studied the microstructure and electrical properties of porous
BST ceramics, they reported that the crystalline structure of the porous BST ceramics
strongly depended on the oxygen content and these ceramics can be used for humidity
and gas sensors [36].
P.Pookmanee et al. (2004), studied the effect of sintering temperature on
microstructure of hydrothermally prepared bismuth sodium titanate ceramics,they
reported that the hydrothermal route has an advantage over other synthesis processing’s,
that BNT powders can be obtained without additional heat treatment. The grain size and
surface densification of BNT ceramics becomes higher and denser with increasing
sintering temperature [37].
H.Miao et al. (2006) reported hydrothermal synthesis, to be considered as one of
the best methods used to prepare mono-disperse nanometer BT powders, which presents
the major advantages: narrow particle size distribution, low concentration, high purity
and fine crystallization of powders, little pollution during the preparation process, short
preparation time and low cost. Fine Dy and Mg-doped BT powders were prepared by
hydrothermal method at 240˚C with BaCl2·2H2O, TiCl4 and NaOH as the main reactants,
Dy2O3 and MgCl2·6H2O as additives respectively. It is confirmed that Dy or Mg enters
into the BT lattice. Ba site is replaced if a little Dy2O3 is doped but some more Dy will
take up the positions of Ti. Mg always substitutes for Ti site. Dy and Mg are both useful
to obtain the microstructure with small grains and high density, and the former results in
a better microstructure [38].
A.Jamil, et al (2007) reported that the ferroelectric capacitors made from BST are
applied as varactors in tunable, high-frequency circuit applications. In that context, a
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 35
voltage-controlled oscillator (VCO) had been designed and implemented using discrete
RF bipolar junction transistor (BJTs) and tunable ferroelectric capacitor [39].
2.4. B-site modification of ABO3:
D.Hennings et al (1982) reported that the very high and broad Curie maxima are
observed in ceramic BZT mixed crystals, which are often used for the preparation of
ceramic dielectrics and studied the ferroelectric-to-paraelectric phase transition of
ceramic BZT using dielectric measurements, XRD, and determination of the Pr. At higher
Zr concentrations, it was found that ferroelectric and paraelectric phases coexist in a wide
temperature region [40].
Z.Yu et al (2000) reported that the successful growth of BZT single-crystal fibers
by the laser-heated pedestal growth technique, a single-phase perovskite structure of the
materials had been identified by the XRD technique. Dielectric properties as function of
temperature and frequency and room-temperature hysteresis loops were measured. Pr and
Ec are obtained and compared for both single crystals and ceramics and observed the
small dielectric relaxation behavior [41].
R.Maier et al. (2001) studied the structural and physical properties of pseudo
cubic thin film BaTi1-xFexO3 grown by pulsed laser deposition. They suggest a substantial
increase of the ferroelectric transition temperature relative to that of bulk BT is to lattice
expansion induced by Fe doping [42].
A. Dixit et al (2002) studied XRD confirmed the structural phases in the powder
and films of BZT and various structural transitions of BT, as a function of different Zr
content, and compared well with the published result on ceramics and single crystalline
BZT. The deposited films were smooth, crack-free and have homogeneous
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 36
microstructure, and Zr content strongly influences the evolution of the microstructures of
the films. Some selected compositions of these films are characterized in terms of their
dielectric properties and phase transition behavior. BZT films with 20% of Zr have
shown a ferroelectric to paraelectric transition in the vicinity of room temperature [43].
Zhi Yu et al (2002) studied the Ferroelectric-relaxor behavior of BZT ceramics in
the temperature range from 150 to 450K and observed broad dielectric peak with a high-
dielectric maximum exhibits frequency dispersion. The polarization hysteresis loops were
observed with a Pr of 10μC/cm2 at 175K. The high- ε and high-polarization properties are
expected to find practical applications at low temperatures [44].
S.Wang et al. (2005) studied the effect of sintering atmosphere on the
microstructure and dielectric properties was endorsed to the change of solubility of the
acceptor ions in this core-shell-structured materials. The core-shell- structure is
considered to be a state of the inhomogeneous grains, in which the unreacted grain core is
pure BT, whereas the shell consists of reacted BT severely doped additives [45].
M.Tanmoy et al (2006) reported that the E-field tunable behavior of the
environmental friendly lead-free perovskite BZT relaxor ceramics in the temperature
range from 300 to 30 K and studied the E dependence of dielectric behavior of the
ceramics, It was shown that manipulating the Zr:Ti concentration in BZT ceramics and
optimizing the applied dc bias field the properties for specific applications in tunable
filters, phase shifters, antennas, etc., can be tailored in the temperature range from
100 to 300 K [46].
B.Li et al. (2007) investigated the microstructure and dielectric properties of Y/Zn
co-doped BT ceramics sintered in reducing atmosphere. They concluded that proper
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 37
amount of Y2O3 and ZnO can notably progress the dielectric temperature characteristics
due to the formation of grain core-shell a structure [47].
Tanmoy Maiti et al (2011) reported that the mechanism and nature of relaxor
ferroelectric behavior in the environmental friendly lead free BZT system. A revised
complete phase diagram of BZT, with different compositions has been developed based
on their electrical properties. Two different kinds of relaxor behaviors have been
observed in the BZT system; one is dominated by polar Ti-rich regions and another by
non-polar Zr-rich regions. All the BZT relaxor compositions are characterized by
dielectric properties with and without bias, pyroelectric and thermal expansion
measurements in the wide range of temperatures. The structure of the BZT compositions
has been evaluated by XRD, Neutron diffraction study. Further the local structure of the
BZT compositions has been probed by micro-Raman spectra. Although the global
structure of BZT relaxors is cubic as observed in Neutron diffraction studies, the local
symmetry is non-cubic as evident in the micro-Raman spectra of BZT relaxors as well as
in their thermal strain measurement, dielectric and pyroelectric behavior [48].
2.5. A-site and B-site modification ofABO3:
L.C.Sengupta et al (1995) reported that BST doped with MgO, has low ε,
extremely low Tan δ and high η such novel materials possess superior electronic
properties; and they may be employed in various antenna systems at both μw and
millimeter wave range frequencies [49].
P.Hansen et al (1998) studied the dielectric properties of (Ba,Ca)(Ti,Zr)O3
ceramics containing various acceptor and donor dopants on the B sites and observed that
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 38
all acceptors cause a reduction of the Curie point and the maximum ε increases with the
average grain size almost independent of the acceptor incorporated [50].
M.W.Cole et al (2000) investigated the structural, microstructural, interfacial, and
surface morphological properties of BST doped with Mg, determined dielectric and
insulating characteristics. Single phase solid solution films were achieved at Mg doping
levels up to 5 mol%, while multiphased films were obtained for 20 mol%. Decreases in
the ε, Tan δ, η and leakage current characteristics were paralleled by a reduction in grain
size with increasing Mg dopant concentration and suggest that Mg doping serves to limit
grain growth and responsible for lowering the ε, Mg behaves as an acceptor-type dopant
at the grain boundary and is responsible for the low Tan δ and good leakage current
characteristics, reported the performance-property trade-offs advocates the 5-mol% Mg
doped BST film to be an excellent choice for tunable μw device applications [51].
Y.Tsur et al. (2001) investigated the rare earth cation substitutions into BT.
Analysis based upon crystal chemistry, defect chemistry and meta stable states is resented
to aid interpretation of experimental data. The detailed and highly precise XRD and
Electron Paramagnetic resonance experiments performed on samples produced with
different A/B ratios and fired under different oxygen partial pressure conditions give rise
to new insights into the material. Specifically, the site occupancy and the valence states
for the rare-earth dopants in BT are considered [52].
M.W.Cole et al (2002) analyzed by glancing angle XRD, SEM, AFM, and Auger
electron spectroscopy studies and measured the dielectric properties of un patterned films
at 10GHz using a coupled, tuned split dielectric resonator system, and at 100kHz using
metal–insulator–metal capacitors on the influence of low concentration of Mg doping on
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 39
the structural, microstructural, surface morphological, and dielectric properties of BST
thin films and shows The Mg-doped BST films exhibited improved dielectric and
insulating properties compared to the undoped BST thin films. The improved dielectric
properties, low leakage current, and good dielectric η of the low level Mg-doped BST
thin films merits strong potential for utilization in tunable μw devices [53].
K.Imai et al (2002) observed that Fe doping of BST films to be remarkably
effective for suppressing the decrease in and investigated the site where the doped Fe
ions are substituted in the crystal by means of electron standing wave method using
SrTiO3 single crystal, reported that most of the Fe ions are substituted at B sites (Ti sites),
which suggests that Fe ions as acceptors compensate donor electrons and reduce band
bending [54].
L.Radhapiyari et al (2003) studied the structural and the microstructural
properties of BST system substituted with iron by varying the amount of Ba and Sr and
investigated the dielectric properties of the system Ba1−xSrxFe0.01Ti0.99O3 as a function of
temperature, frequency and dc bias. The η of the system shows up to 42% for a particular
composition with Ba/Sr ratio of 70:30 [55].
X.F.Liang et al (2003) investigated the effect of doping Al2O3 on the BST
ceramics. A strong correlation was observed between the average grain size and Al2O3
content,shows the Tan δ and tunable properties of modified BST. The minimum of the
Tan δ was achieved at Al2O3 doping level up to 0.8 wt.% and obtained the maximum η of
30.1% at the doping level of 0.4 wt.% Al2O3 [56].
X. F. Liang et al (2004) investigated the effects of different concentrations of
Mn2+
, Mg2+
, Al3+
, Fe3+
, La3+
, and Nb5+
on the dielectric and tunable properties of BST
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 40
ceramics. It was observed that doping in small amounts with acceptor ions such as Mg2+
,
Fe3+
, and Al3+
could meliorate the dielectric properties clearly, Decrease of Tan δ was
attributed to the formation of compensating defects originating from acceptor substitution
and reported that the η was linked to both the ε and the grain size [57].
L.C.Sengupta et al (2004) reported that the electronically tunable materials
include an electronically tunable dielectric phase such as BST in combination with at
least two additional metal oxide phases. The additional metal oxide phases may include,
for example, oxides of Mg, Si, Ca, Zr, Ti and all such tunable materials are used in
devices such as phased array antennas, tunable filters also useful in many applications,
including the area of RF engineering and design [58].
K.T.Kim et al (2005) studied the effect of Cr doped BST prepared from alkoxide-
based sol–gel method on the Pt/Ti/SiO2/Si substrate. AFM and XRD analyzed and
showed that increasing the Cr-doping ratio causes increased grain size while the surface
remains smooth and crack-free. It was also reported that BST improves the and the
leakage-current characteristics, the figure of merit reached the maximum value of 72.3 at
the 5 mol% of Cr doping. Cr-doped BST thin films are prospective candidates for
applications in tunable devices [59].
Y.Chen et al (2005) investigated that the dielectric properties of BSTO/Mg2SiO4/
MgO composite ceramics. It was suggested that the dielectric properties were influenced
to a great extent by the microstructure, and the η [60].
Q-Y Shao et al (2006) investigated that the Tc of Pb1−xSrxZr0.52Ti0.48O3 [(PSZT)
x=0.2–0.8] decreases with the increase of Sr contents and paraelectric PSZT films at
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 41
room temperature are demonstrated and the increase of Sr contents also leads to the
simultaneous decrease of ε, η and Tan δ [61].
R.X.Li et al (2006) investigated the dielectric response and tunable properties of
Cr-doped BST solid solution, observed that all of the doped specimens are cubic
perovskite phase, grain size increases with the increase of Cr content below 0.6 mol%,
The dielectric frequency spectra of the doped BST solid solution showed that an
additional relaxation of the doped specimens is observed at frequencies above 10 MHz
and shows that η and Tan δ were improved by doping with Cr concentration lower than
1.0 mol% compared with un doped material. The 0.6 mol% Cr-doped specimen reveals a
maximum η and figure of merit of 23.3% and 518.3, respectively. Extremely low Tan δ
in order of 5 × 10−4
is found for 0.4–0.6 mol% Cr-doped BST solid solution. The
dramatically low Tan δ of the specimen is explained by the reducing of Cr3+
to Cr2+
and
the acceptor action of Cr3+
and Cr2+
which neutralized the donor action of oxygen
vacancies [62].
X.J.Chou et al (2007) prepared BST-Mg2TiO4 composite ceramics via the
conventional solid-state reaction method. The microstructures, η, and μw properties of
composite ceramics were investigated. The ε is tailored from 335 to 35 by manipulating
the addition of Mg2TiO4 from 50% to 80% weight ratio and the η was 10.8% measured at
10 kHz for the 80% Mg2TiO4 addition. The composite ceramics with high Q value (>200)
are useful for potential tunable μw device applications in the wireless communication
system [63].
U.C.Chung et al (2008) reported that Spark plasma sintering (SPS) was an
efficient tool to obtain highly densified ferroelectric-dielectric ceramic composites with
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 42
clean interfaces and tunable properties. Dielectric MgO and ferroelectric BST were
combined in two-dimensional multilayer and three-dimensional random powders design.
Such SPS ceramics can be used as experimental input for simulation and were potential
candidates for high frequency applications [64].
2.6. Rare earth material modified ABO3:
A.Yamaji et al. (1977) studied preparation, characterization and properties of Dy-
doped BT ceramics. The effect of grain size on dielectric constant, lattice parameters and
linear thermal expansion coefficient are more pronounced than the chemical effects of Dy
doping in the ferroelectric state [65].
W.H.Su et al. (1986) synthesized and investigated double rare earth oxides of
ABO3 composition. Their analysis focused on the crystal structure of the compound
which was synthesized by using high pressure and high temperature methods [66].
A.S.Shaiks (1986) studied the structure and dielectric properties of BT doped with
Nd2O3 . Their results illustrated that Nd occupies the Ba2+
site and charge compensation
takes place by creation of Ti4+
vacancies. The addition of Nd2O3 leads to very drastic
shift in the Tc of BT [67].
E.Iguchi et al. (1991) synthesized La2O3, Gd2O3 doped BT, and studied their
dielectric and conductivy properties. They concluded theoretically, that the dominant
conduction in n-type BT is due to hopping motion of non-adiabatic polarons [68].
C.Eylem et al. (1992) reported the synthesis and properties of RxBa1-xTiO3 series
where R = La, Gd, Nd, Er and Y. These compounds display rare earth dependent metal to
semiconductor transition that co relate with the perovskite tolerance factor. Atomic
absorption and TGA of these samples were also studied [69].
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 43
M.Kuwabara et al. (1997) observed that with an increase in sintering temperature,
the rate of increase of Tc in La-doped BT ceramics increases. A phase transition
phenomenon was interpreted based on concentration change of lanthanum in the lattice
defects present in the material with sintering temperature. A distinct increase in the room
temperature bulk resistivity with an increase in sintering temperature was also observed
[70].
F.D.Morison et al. (1998) reported a novel doping mechanism comprising A-site
doping with creation of Ti vacancies for very high ε BT ceramics. A typical value of ε
10,000 at 130°C in undoped BT was reported with Tc 226
°C [71].
F.D.Morison et al. (1999) investigated ε of La3+
doped BT ceramics. They
obtained ε at the phase transition of 130°C for x = 0 and – 9
°C for x = 0.06 sampled fired
in O2 atmosphere were insulating and showed no signs of donor doping, whereas air fired
samples were semiconducting attributed to oxygen loss [72].
S.Urek et al. (2000) studied the electrical properties of La3+
doped BT samples
with donor concentration in the range from 0.3 to 12.5 mol% of La, results showed that
with the use of specific sintering profile PTCR ceramics containing an amount of donor
dopants >0.3 mol%, can be prepared [73].
D.Li et al. (2000) have prepared Ba1-xLnxTi1-xMxO3 (Ln=La, Sm, Gd, Dy. M=Al,
Fe, Cr) the tunable ferroelectric compositions ceramics and shown that, the simultaneous
doping of acceptor and donor ions in their polycrystalline BT can shift the Tc to a lower
temperature and increase the η [74].
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 44
T.Nagai et al. (2000) discussed the effect of MgO doping in the phase
transformation in BT. A change in Raman spectra with temperature showed that
orthorhombic to rhombohedral phase exist at high temperature [75].
F.D.Morrison et al. (2001) investigated the mechanism of doping BT with La by a
combination of XRD, electron probe microanalysis, scanning and transmission electron
microscopy and impedance measurements. Phase diagram results confirm that the
principal doping mechanism involves ionic compensation through the creation of titan-
ium vacancies. The change from insulating to semiconducting behavior is reversible, by
changing the atmosphere on heating at 1350 – 1400˚C [76].
Y.Tsur et al. (2001) studied issue of rare earth (Lu3+
-La3+
) cation substitutions in
BT. They have analyzed the crystal and defect chemistry with the formation of metal
state in their structural characteristics. EPR measurement shows the site occupancy of
various dopants along with their valence states. The nature of amphoteric ions defect and
site occupancy was also reviewed and compared with the early study [77].
J.H.Wang et al. (2001) reported that an electrical property of Ce-doped BT. The
Tc lowered when Ce3+
is incorporated in Ba site where as the substitution of Ce4+
for Ti4+
sites resulted in no change in Tc. There is no significant change in conductivity behavior
when compared with pure BT, clearly indicating the substitution of tetravalent Ce at Ti-
site of Ce doped BT ceramics [78].
A.M.Slipenyuk et al. (2001) prepared BT ceramics doped by Y and Ca and has
been studied by electron spin resonance (ESR). They reported that the grain size of BT
ceramics became smaller under Ca doping though the temperature region of the effect of
PTCR remain practically unaffected [79].
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 45
M.T.Buscaglia et al. (2002) investigated Er3+
substitution in BT ceramics by
having dopant concentration in the range 0.2, 0.5 and 10% Er3+
solubility at the Ba site
does not exceed,. However the resulting properties such as electrical conductivity were
sensitive to sintering condition [80].
M.B.Park et al.(2003) demonstrated that the chemical and electrical features of
the ceramics with grain boundary can be controlled and designed based on the diffusion
coefficient as well as grain boundary potential barrier height at particular heat-treatment
conditions [81].
J.Du et al. (2004) prepared the Ni/Graphite/BT composites are fabricated by
adding Ni and Graphite powders in to BT ceramics. They reported that the room
temperature resistivity of the composites is much lower than the prototype ceramics. The
magnitude of resistivity changes to some extent. Graphite added will prevent the
oxidation of Ni, but a lot of pores will be produced in the bulk with overdose of graphite
so that the resistivity of the composites increases subsequently [82].
Z.C.Li, et al. (2005) prepared Sm2O3 doped BT ceramics with a PTCR by solid
state reaction sintering. The grain size decreased with increasing dopant content
secondary phase and lattice parameters a = 10.6Å and c = 20.2Å formed in the ceramics.
The room temperature resistivity decreases with the increase of dopant content in the low
doping level and reaches the minimum value at a certain dopant content (about 0.2
mol%), then increases with the increasing of dopant content [83].
S.Qizhen et al. (2005) reported that the conventional doping method of solid
doping is associated with many disadvantages including the high impurity, poor powder
characteristics and compositional inhomogeneity. Thus, some authors have began to
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 46
prepare BT doped with additives using sol-gel processing by one step, which has many
advantages such as high purity and good distribution. But until now, few papers report
the influence of Ti/Ba ratio on the microstructure and dielectric property of rare earth
doped BT the Ti/Ba ratio of the samples significantly influences the ceramics'
microstructures. The Nd-doped BT nano crystalline powders and ceramics with different
Ti/Ba ratios were prepared by sol-gel method. Phases and microstructures of the Nd-
doped BT based powders and ceramics were characterized by XRD, SEM and TEM
methods. The results revealed that the powders synthesized by sol-gel method were
nanometer scale (30-60nm) and were mainly composed of cubic BT with a small amount
of BaCO3. After sintering at high temperature, both cubic BT, and BaCO3 were
transformed into tetrahedron BT phase [84].
S.Sen et al. (2005) polycrystalline sample of (Ba1-xCax) (Sn0.15Ti0.85) O3 (x = 0,
0.03, 0.06 and 0.09) of perovskite structure family have been prepared by a high
temperature solid state reaction technique. Dielectric studies shows the compound
undergo diffuse phase transition. DC and AC conductivities have been investigated over
a wide range of temperature and the activation energy was also calculated [85].
Z.Yumin et al. (2006) investigated the effect of Ce3+
and Eu3+
doping on the
structure, the microstructure and dielectric properties of BT ceramics. Ce-doped BT
exhibit pseudo-cubic perovskite structure while Eu doped BT ceramics exhibit tetragonal
perovskite structure [86].
Da-Young Lu et al. (2006) explained the role of Co-doping with La and Ce for
the first time in BT ceramics. Co-doping with lanthanum and Ce causes a strong
broadening of ferroelectric phase transition and resist the Curie peak, with rapid shift
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 47
these materials are promising candidate for future Y5V monolithic or even X7R MLCC
[87].
R.K.Dwivedi et al. (2007) have investigated the ferroelectric transition in valance
compensated Ba1-xLaxTi1-xCrxO3 ceramics. They reported that dielectric anomaly
corresponding to the ferroelectric to paraelectric transition has been found to shift the
lower temperature with the increase in concentration of La and Cr [88].
P.Yongping et al. (2007) showed the influence of rare-earths on electrical
resistivity and microstructure of BT ceramics doped with rare-earth ions Y, Dy, Ho, Er
and Y. Their result showed that a dramatic decrease in the resistivity occurred at the
concentration of 0.3% of La doped sample. However the range of concentration for
semiconducting samples doped with Dy, Ho, Er and Y was wider especially for Y-doping
[89].
E.Aizinger et al. (2007) studied the solubility of Pr in BT.The two series of
samples were investigated. First one was Ba-rich series and the second one had Ba/Ti
ratio equals 1. In Ba-rich series, it was found that the solubility limit is between 4 mol%
and 10 mol% Pr. In the second series the solubility limit was between 15 mol% and 20
mol% Pr [90].
L.Lingxia et al. (2007) studied the doping effect of Gd2O3 on BT based meta-
dielectric composite ceramics system was studied, that the doping effect of Gd2O3 could
restrain the growth of grain which could make the dimension of grain and small and
density high it could be broadened the Curie peak of the ceramics and increases at room
temperature. The replacement of B-sites by Gd3+
could lead some non ferroelectric areas
[91].
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 48
J.Zhang et al. (2008) prepared the BST with 0.5 mol% of various trivalent rare-
earth elements ceramics. Their structural and dielectric properties are studied. The XRD
pattern displays the addition of rare-earth changes the structure from cubic to tetragonal
and improve the tetragonality distortion of BST and rare earth element is found to be an
important factor in controlling the temperature dependency of the dielectric properties.
Due to their low ε, low Tan δ and moderate η, the Sm, Eu, Gd-doped samples are very
attractive for the tunable μw devices [92].
Z.Yao et al. (2008) investigated the structure and dielectric behavior of Ba1-
xNdxTiO3 perovskite fabricated by solid state mixed method. By increasing Nd doping
phase transition behavior appeared from tetragonal to cubic structure. Nd3+
addition
shifted the temperature of the ε maximum and decreases the grain size [93].
Y. B. Xu et al (2008) prepared BST-Sr(Ga0.5Ta0.5)O3 solid solutions by solid-state
reaction method, and investigated their dielectric and tunable characteristics. It was
observed that the addition of Sr(Ga0.5Ta0.5)O3 into BST causes a shift in the phase
transition peak to a lower temperature, depressed and broadened phase transition peaks,
resulted in decreased ε and Tan δ at room temperature. With the increase of Sr
(Ga0.5Ta0.5) O3 content, the ε, Tan δ, and η are decreased [94].
Y.Li et al. (2009) has prepared Sm doped BST ceramics, and investigated the
dielectric properties. They found that the substitution of Sm3+
for the host cations
perovskite lattice. Owing to the replacement of Sm3+
ions for A-site, Tc rises with the
increase of Sm2O3 doping when the doping content is below 0.1 mol%, meanwhile when
the content is more than 0.1 mol%, Sm3+
ions tend to occupy the B-site, causing a drop of
Tc. Owing to the modification of Sm3+
doping, more over the creation of oxygen
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 49
vacancies controls the ε when the addition is above 0.1 mol%, so the ε decreases with
increase of Sm3+
[95].
S.B.Reddy et al.(2009) studied the effect of La substitution on the structure and
dielectric properties of BZT ceramics. The ε maximum was observed at 2 mol% La
substitutions and with further increase in La content the phase transition was found to be
broad [96].
P.Pasierb et al. (2011) reported the barium create exhibits high protonic
conductivity, especially when doped by suitable trivalent ions. A possible approach to get
the protonic conductor stable in the presence of CO2 with relatively high protonic is the
preparation of solid solutions BaCe1-xMexO3-δ (Me = Zr, Ti) doped simultaneously with
acceptor ion [97].
P.Kumar et al. (2011) were synthesized Ba0.80-xCaxPb0.20Ti0.90Zr0.10O3 ceramics by
solid state reaction. Samples microstructure and dielectric, ferroelectric piezoelectric
properties studied. They reported that Tan δ was found to improve with increase in x
where piezoelectric charge coefficient d33 was found to decrease with increase in x [98].
Thus, with this review of literature, we have focused our attention on the
following aims and objectives:
Aims and objectives of the work:
The main aim of this work is to prepare modified dielectric ceramics and study
their tunable properties.
Following are the major objectives planned for this work:
1. Synthesis of BSZT in the form of (Ba0.6Sr0.4)(Zr1-xTix)O3 (x=0.40, 0.50 and 0.65) and
Modified BSZT with the stoichiometric (Ba0.6Sr0.4)(Zr0.6Ti0.4)O3-Nb2O5-Fe2O3-RE
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 50
(where, RE=La2O3, Gd2O3 ,Nd2O3, Sm2O3, HO2O3. Pr2O3, Er2O3).
2. Study of structural, micro-structural and surface morphology of synthesized
compounds.
3. Study of temperature and frequency dependent electrical and dielectric behavior in
order to understand their DPT, ferroelectric and tunable properties.
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 51
References:
1. C.Kittel, “Introduction to solid state physics”, 7th Edition, John Wiley and sons,
New York (1995)
2. G.Sirane, S.Hoshino, K.Suzuki, “Crystal structure of lead titanate and of lead-
barium titanate”, J. Phys. Soc., Japan, 5 453-455 (1950)
3. B.Jaffe, W.Cook, H.Jaffe, “Piezoelectric ceramics”, Academic Press, London, 3120
(1971)
4. A.Safari, R.K.Panda, V.F.Janas, “Ferroelectric ceramics: processing, properties
and applications”, J. Am. Ceram. Soc., 4 82-90 (2006)
5. H.Diamond, “Variation of permittivity with electric field in perovskite like
ferroelectrics”, J. Appl. Phys., 32 909-915 (1961)
6. K.M.Johnson, “Variation of dielectric constant with voltage in ferroelectrics and
its application to parametric devices”, Appl. Phys., 33 2826-2831 (1962)
7. K.Uchino, E.Sadanaga, K.Oohashi, T.Morohashi, H.Yamamura, “Particle/grain size
dependent of ferroelectricity”, Ceram. Trans. 8 107-115 (1989)
8. K.Uchino, E.Sadanaga, T. Hirose, “Dependence of the crystal structure on particle
size in barium titanate”, J. Am. Ceram. Soc., 72 1555-58 (1989)
9. A.I.Kingon, S.K.Streiffer, C.Basceri, S.R.Summerfelt, “(Ba,Sr)TiO3 dielectrics:
relationship between bulk and thin film properties”, US-Japan Seminar on
Dielectric and Piezoelectric Ceramics, (1999)
10. H.Takasu, “The ferroelectric memory and its applications”, J. Electroceram. 4
327-331 (2000)
11. S.B.Park, W.K.Choo, “Structural and dielectric studies of the phase transitions in
Pb(Yb1/2Ta1/2)O3-PbTiO3 ceramics”, Jpn. J. Appl. Phys., 39(9B) 5560-5564 (2000)
12. E.Tuncer, Y.V.Serdyuk, S.M.Gubanski, “Dielectric mixtures: Electrical Properties
and modelling”, IEEE Trans. on Dielectrics and Electrical Insulation, 9(5) 809-828
(2002)
13. C.D.Dimitrakopoulos, P.R.L.Malentant, “Organic thin film Transistors for Large
area electronics”, Adv. Mater., 14 99-117 (2002)
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 52
14. K.F.Astafiev, V.O.Sherman, A.K.Tagantsev, N.Setter, “Can the addition of a
dielectric improve the figure of merit of a tunable material”, J. Eur. Ceram. Soc.,
23 2381-2386 (2003)
15. A.K.Tagantsev, V.O.Sherman, K.F.Astafiev, J.Venkatesh, N.Setter, “Ferroelectric
materials for microwave tunable applications”, J. Electroceram., 11 5-66 (2003)
16. V.Buscagliaa, M.Viviania, M.T.Buscagliaa, P.Nannib, L.Mitoseriub, A.Testinob,
“Nanostructured barium titanate ceramics”, Powder Tech., 148 24-27 (2004)
17. M.Cernea, “Sol-gel synthesis and characterization of BaTiO3 powder”, J. Opto-
electro. and Adv. Mater. 7 3015-3022 (2005)
18. C.Pithan, D.Hennings, R.Waser, “Progress in the synthesis of nanocrystalline
BaTiO3 powders for MLCC”, Int. J. Appl. Ceram. Tech., 2(1) 1-14 (2005)
19. A.Sreenivasalu, T.N.V.K.V.Prasad, S.Buddhudu, “Synthesis and characterization
of BaTiO3 and LiNbO3 ceramic powders”, Ind. J. Pure and App. Phy., 45 741-744
(2007)
20. F.F.Hammad, A.K.Mohamed, A.M.Ei-Shabiny, “X-ray diffraction study on
structural characteristics of pure and doped perovskite BaTiO3”, Egypt. J.
Solids., 31(1) (2008) 55
21. W.Li, Z.Xua , R.Chu, P.Fu, J. Hao, “Surface mechanical attrition treatment
induced phase transformation behavior in Ni-Ti shape memory alloy”, J. Alloys
Comp., 482 137-147 (2009)
22. E.E.Oren, A.Cuneyttas, “Hydrothermal Synthesis of Dy-doped BaTiO3 powders”,
Metallurg. and Mater. Transac. B., 30b 1089-1093 (1999)
23. C.Pithan, Y.Shiratori, R.Waser, J.Dornseiffer, F. H. Haeghee, “Preparation,
processing and characterization of nano-crystalline BaTiO3 powders and
ceramics derived from microemulsion-mediated synthesis”, J. Am. Ceram. Soc.,
89(9) 2908-2916 (2006)
24. Y.Mao, S.Mao, Z.G.Ye, Z.Xie, L.Zheng, “Solvothermal synthesis and Curie
temperature of monodispersed barium titanate nanoparticles”, Mater. Chem.
Phys., 124 1232-1238 (2010)
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 53
25. R.N.Viswanath, S.Ramasamy, “Preparation and ferroelectric phase-transition
studies of nanocrystalline BaTiO3 nano-structured materials”, Nano Structured
Mater., 8 155-162 (1997)
26. P.K.Panda, “Review: environmental friendly lead-free piezoelectric materials”, J.
Mater. Sci., 44 5049-5062 (2009)
27. Ching-Fang Tseng, Cheng-Hsing Hsu, “A New compound with ultra low dielectric
loss at microwave frequencies”, J. Am. Ceram. Soc., 92 1149 (2009)
28. Takashi Teranishi, Takuya Hoshina, Hiroaki Takeda, Takaaki Tsurumi, “Analysis of
polarization behavior in relaxation of BaTiO3-based ferroelectrics using
wideband dielectric spectroscopy”, IEEE Trans. Ultrason. Ferroelec. and Freq.
Cont. 57 2118-2126 (2010)
29. I.M.Reaney, E.Colla, N.Setter, “Dielectric and structural characteristics of Ba-
and Sr-based complex perovskites as a function of tolerance factor”, Jpn. J. Appl.
Phys., 33 3984-3990 (1994)
30. L.C.Sengupta, S.Sengupta, “Breakthrough advantages in low loss, tunable
dielectric materials”, Mater. Res. Innovat. 2 278-282 (1999)
31. P.H.Chen, C.C.Chou, H.F.Cheng, C.T.Hu, I.N.Lin, “Microstructural
characteristics and nonequilibrium core-shell phase in (PbxSr1−x)TiO3 materials
and their electrical properties”, Ferroelectric 241 25-32 (2000)
32. S.Ezhilavan, T.Y.Tseng “Progress in the developments of (Ba,Sr)TiO3 (BST) thin
films for gigabit era DRAMs”, Mater. Chem. Phys. 65 227-363 (2000)
33. R.Wanga, Y.Inagumabb, M.Itoha “Dielectric properties and phase transition
mechanisms in Sr1-xBaxTiO3 solid solution at low doping concentration”, Mater.
Res. Bul., 36 1693-1701 (2001)
34. B.D.Stojanovic, C.R.Foschani, T.V.Sreckovic “Structural and electrical
characterization of semiconducting barium-lead-titanate ceramics”,
Ferroelectrics, 32 73-82 (2001)
35. D.Shiwen, W.Jing, Q.Jianglei, L.Ximao, “Hydrothermal synthesis, structure and
property of nano-BaTiO3-based dielectric materials”, Science in China (Series B)
44(6) 658-662 (2001)
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 54
36. J.G.Kim, “Synthesis of porous (Ba,Sr)TiO3 ceramics and PTCR characteristics”,
Mater.Chem.Phys., 78 154-159 (2002)
37. P.Pookmaneea, G.Rujijanagulb, S.Anantab, R.B.Heimannc, S.Phanichphanta “Effect
of sintering temperature on microstructure of hydrothermally prepared bismuth
sodium titanate ceramics”, J. Eur. Ceram. Soc., 24 517-520 (2004)
38. H.Miao, M.Dong, G.Tan , Y.Pu “Doping effects of Dy and Mg on BaTiO3ceramics
prepared by hydrothermal method”, J. electroceramics., 16 297-300 (2006)
39. A.Jamil, T.S.Kalkur, N.Cramer, “Tunable Ferroelectric capacitor-based voltage-
controlled oscillator”, IEEE Trans. Ultrasonic Ferroelec. and Freq. Cont., 54 222-
226 (2007)
40. D.Hennings, A.Schnell, G.Simon, “Diffuse ferroelectric phase transitions in
Ba(Ti1-yZry)O3 ceramics”, J. Am. Ceram. Soc., 65 539-544 (1982)
41. Z.Yu, R.Guo, A.S.Bhalla, “Dielectric behavior of Ba(Ti1−xZrx)O3 single crystals”,
J. Appl. Phys., 88 410-415 (2000)
42. R.Mair, J.L.Cohn, J.J.Neumeier, L.A.Bendersky “Ferroelectricity and
ferrimagnetismin iron-doped BaTiO3”, Appl. Phys. Lett., 78(17) 2536-2538
(2001)
43. A. Dixit, S.B. Majumder, A. Savvinov, R.S. Katiyar, R. Guo, A.S. Bhalla,
“Investigations on the sol–gel-derived barium zirconium titanate thin films”,
Mater. Let., 56 933-940 (2002)
44. Zhi Yu, Chen Ang, R. Guo, A. S. Bhalla, “Ferroelectric-relaxor behavior
of Ba(Ti0.7Zr0.3)O3 ceramics”, J. Appl. Phys. 92 2655-2657 (2002)
45. S.Wang, S.Zhang, X.Zhou, B.Li, Z.Chen, “Effect of sintering atmospheres on the
microstructure and dielectric properties of Yb/Mg co-doped BaTiO3 ceramics”,
Mater. Lett., 59 2457-2460 (2005)
46. M. Tan moy, R. Guo, A. S. Bhalla, “Electric field dependent dielectric properties
and high tunability of BaZrxTi1−xO3 relaxor ferroelectrics”, Appl. Phys. Lett., 89
122909 (1-3) (2006)
47. B.Li, S.Zhang, X.Zhou, Z.Chen, S.Wang, “Hydrothermally stable aluminosilicate
mesostructures prepared from zeolite ZSM-5”, J. Mater. Sci., 42 401-405 (2007)
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 55
48. Tan moy Maiti, R.Guo, A.S.Bhalla, “Evaluation of experimental resume of
BaZrxTi1-xO3 with perspective to ferroelectric relaxor family: An overview”,
Ferroelect., 425 4-26 (2011)
49. L.C.Sengupta, E.Ngo, M.E.O’Day, S.Stowell, R. Lanco, “Ceramic ferroelectric
composite material - BSTO-MgO”, U. S. Patent, 5427988 (1995)
50. P. Hansen, D. Hennings, H. Schreinemacher, “ High-K dielectric ceramics from
donor/acceptor-codoped (Ba1-xCax) (Ti1-yZry)O3 (BCTZ)”, J. Electroceram., 2
1363-1379 (1998)
51. M.W.Cole, P.C.Joshi, M.H.Ervin, M.C.Wood, R.L.Pfeffer, “The influence of Mg
doping on the materials properties of Ba1−xSrxTiO3 thin films for tunable device
applications”, Thin Solid Films, 374 34-41 (2000)
52. Y.Tsur, T.D.Dunbar, C.A.Randalli, “Crystal and defect chemistry of rare earth
cations in BaTiO3”, J. Electro. Ceram., 7 25-34 (2001)
53. M.W.Cole, C.Hubbard, E.Ngo, M.Ervin, M.Wood, R.G.Geyer, “Structure–
property relationships in pure and acceptor-doped Ba1−xSrxTiO3 thin films for
tunable microwave device applications”, J. Appl. Phys., 92 475-483 (2002)
54. K.Imai, S.Takeno, K.Nakamura, “Effect of Fe doping of thin (Ba,Sr)TiO3 films on
increase in dielectric constant”, Jpn. J. Appl. Phys. 41 6060-6064 (2002)
55. L.Radhapiyari, O.P.Thakur, C.Prakash, “Structural and dielectric properties of the
system Ba1-xSrxFe0.01Ti0.99O3”, Mater. Lett., 57 1824-1829 (2003)
56. X.F.Liang, W.B.Wu, Z.Y.Meng, “Dielectric and tunable characteristics of barium
strontium titanate modified with Al2O3 addition”, Mater. Sci. Eng. B, 99 366-369
(2003)
57. X.F.Liang, Z.Y.Meng, W.B.Wu, “Effect of acceptor and donor dopants on the
dielectric and tunable properties of barium strontium titanate”, J. Amer. Ceram.
Soc. 87 2218-2222 (2004)
58. L.C.Sengupta, X.Zhang, L.H.Chiu, “Ceramic ferroelectric composite material
BSTO-MgO”, U. S. Patent, 6774077 (2004)
59. K.T.Kim, C.I.Kim, “The effect of Cr doping on the microstructural and dielectric
properties of (Ba0.6Sr0.4)TiO3 thin films”, Thin Solid Films, 472 26-30 (2005)
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 56
60. Y.Chen, X.L.Dong, R.H.Liang, J.T.Li, Y.L.Wang, “Dielectric properties of
Ba0.6Sr0.4TiO3/Mg2SiO4/MgO composite ceramics”, J. Appl. Phys., 98 064107
(2005)
61. Q-Y Shao, A-D Li, Y-D Xia, D.Wu, Z-G Liu, N-B Ming, “Strontium-modified lead
zirconate titanate thin films for electrically tunable device applications”, J. Appl.
Phys. 100 036102(1-3) (2006)
62. R.X.Li, J.R.Cheng, Z.Y.Meng, W.B.Wu, “Low dielectric loss and enhanced
tunable properties of Cr-doped barium strontium titanate solid solution”, J.
Mater. Sci: Mater. Electron., 17 587-596 (2006)
63. X.J.Chou, J.W.Zhai, X.Yao, “Dielectric tunable properties of low dielectric
constant Ba0.5Sr0.5TiO3-Mg2TiO4 microwave composite ceramics”, Appl. Phys.
Let., 91 122908 (1-3) (2007)
64. U.C.Chung, C.Elissalde, M.Maglione, C.Estournes, M.Pate, J.P.Ganne, “Low-losses,
highly tunable Ba0.6Sr0.4TiO3/MgO composite”, Appl. Phys. Let., 92 042902(1-3)
(2008)
65. E.A.Nenasheva, N.F.Kartenko, I.M.Gaidamaka, O.N.Trubitsyna, S.S.Redozubov,
A.I.Dedyk, A.D.Kanareykin, “Low loss microwave ferroelectric ceramics for high
power tunable devices”, J. Eur. Ceram. Soc., 30 395-400 (2010)
66. A.Yamaji, Y.Enomoto, K.Kinoshita, T.Murakami, “Hydrothermal synthesis of Dy-
doped BaTiO3 powders”, J. Am. Ceram. Soc., 60(3–4) 97-101 (1977)
67. A.S.Shaiks, R.W.Vest, “Defect structure and dielectric properties of Nd2O3-
modified BaTiO3”, J. Am. Ceram. Soc., 69(9) 689-694 (1986)
68. E.Iguchi, N.Kubota, T.Nakamori, N.Yamamoto, K.J.Lee, “Polaronic conduction
in n-type BaTiO3 doped with La2O3 or Gd2O3”, Phys. Rev., 10 8646-8649 (1991)
69. C.Eylem, G.Saghi-Szabo, B.H.Chen, B.Eichhorn, J.L.Peng, R.Greene, L.Salamanca-
Riba, S.Nahm, “Structural, magnetic and transport properties of RxBa1-
xTiO3 solid solutions: rare earth dependent metal insulator transitions”, Chem.
Mater., 4(5) 1038-1046 (1992)
70. M.Kuwabara, H.Matsuda, “Sintering temperature”, J. Am. Ceram. Soc., 80(10)
2590-2596 (1997)
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 57
71. F.D.Morrison, D.C.Sinclair, J.M.S.Skakle, A.R.West, “Novel doping mechanism for
very-high-permittivity barium titanate ceramics”, J. Am. Ceram. Soc., 81(7)
1957-1960 (1998)
72. F.D.Morrison, D.C.Sinclair, A.R.West, “Electrical and structural characteristics of
lanthanum-doped barium titanate ceramics”, J. Appl. Phys., 86(11) 6355-6366
(1999)
73. S.Urek, M.Drofnik, D.Makovec, “Sintering and properties of highly donor-doped
barium titanate ceramics”, J. Mater. Sci., 35 895-901 (2000)
74. D.Li, M.A.Subramanian, “Noval tunable ferroelectric compositions:
Ba1−xLnxTi1−xMxO3 (Ln=La, Sm, Gd, Dy. M=Al, Fe, Cr)”, Solid State Sciences, 2
507-512 (2000)
75. T.Nagai, K.Iijima, “Effect of MgO doping on the phase transformations of
BaTiO3”, J. Am. Ceram. Soc., 83(1) 107-112 (2000)
76. F.D.Morison, A.M.Coats, D.C.Sinclair, A.R.West, “Charge compensation
mechanisms in La doped BaTiO3”, J. Electroceram., 6 219-323 (2001)
77. Y.Tsur, T.D.Dunbar, C.A.Bandall, “Crystal and defect chemistry of rare earth
cations in BaTiO3”, J. Electroceram., 7(1) 25-34 (2001)
78. J.H.Hwang, Y.H.Han, “Electrical properties of cerium-doped BaTiO3”, J. Am.
Ceram. Soc., 84(8) 1750-1754 (2001)
79. A.M.Slipenyuk, M.D.Glinchuk, I.P.Bykov, V.V.Lagutaa, S.N.Nokhrin, A.G. Belous,
V.Yunov, L.L.Kovlenko, L.Jastrabik, “Atomistic Simulation of dopant
incorporation in barium titanate”, J. Am. Ceram. Soc., 254 349-355 (2001)
80. M.T.Buscaglia, M.Viviani, V.Buscaglia, C.Bottino, “Incorporation of Er3+
into
BaTiO3”, J. Am. Ceram. Soc., 85(6) 1569-1575 (2002)
81. M.B.Park, S.J.Hwang, N.H.Cho, “Effect of the grain size and chemical features on
the phase transition and physical characteristics of nano-grained BaTiO3
ceramics”, Mater. Sci. Eng., B99 155-161 (2003)
82. D.U.Juan, Q.U.Yuanfang, M.A.Weibing, “Structural model of Ni/ Graphite/
BaTiO3 composites”, J. Electroceram., 12 163-167 (2004)
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 58
83. Z.C.Lia, H.Zhangb, X.Zoub, B.Bergamana, “Synthesis of Sm-doped
BaTiO3 ceramics and characterization of a secondary phase”, Mater. Sci. Engg.
B., 116 34-39 (2005)
84. S.Qizhen, C.Bin, W.Hui, T.Jing, C.H.Zhuguo, H.Yudong, “Nd-doped barium
titanate ceramics with various Ti/Ba ratios prepared by sol-gel method”, Science
in China Ser. B Chemistry., 48 60-64 (2005)
85. S.Sen, R.N.P.Choudhary, “Structural, dielectric and electrical properties of Ca
modified BaSn0.15Ti0.85O3ceramics”, J. Mater. Sci., 40 5457-5465 (2005)
86. Z.Yumin, S.Xiuyun, L.U.Dayong, “Effects of cerium doping at Ti sites and
europium doping at Ba sites on dielectric properties of BaTiO3 ceramics”, Chem.
Res. Chinese U., 22(4) 515-519 (2006)
87. D.Y.Lu, M.Toda, M.Suigeano, “High-permittivity double rare-earth-doped
barium titanate ceramics with diffuse phase transition”, J. Am. Ceram. Soc.,
89(10) 3112-3123 (2006)
88. B.Li, S.Zhang, X.Zhou, Z.Chen, S.Wang, “An analytical model for number of
fibre-fibre contacts in paper and expressions for relative bonded area (RBA)”, J.
Mater. Sci., 42 522-528 (2007)
89. R.K.Dwivedi, O.Prakash, D.Kumar, K.K.Srivastava, P.Singh, “Ferroelectric
transitions in valence compensated Ba1-xLaxTi1-xCrxO3 ceramics”, J. Mater. Sci.,
42 72-79 (2007)
90. P.Yongping, Y.Wenhu, C.Shoutian, “Influence of rare earths on electric
properties and microstructure of barium titanate ceramics”, J. Rare-earths, 25
154-157 (2007)
91. L.Lingxia, G.Rui, Z.Ping, Z.Jing, W.Hongru, “Mechanism of cerium on clearing
superoxide radical”, J. Rare-earths, suppl., 151-154 (2007)
92. J.Zhang, J.Zhai, X.Chou, X.Yao, “Influence of rare-earth addition on
microstructure and dielectric behavior of Ba0.6Sr0.4TiO3 ceramics”, Mater. Chem.
Phys., 111 409-413 (2008)
93. Z.Yao, H.Liu, Y.Liu, Z.Wu, Z.Shen, M.Cao, “Synthesis and characterization of
bimagnetic bricklike nanoparticles”, Mater. Chem. Phys., 20 475-478 (2008)
Preparation And Tunable Properties Of Modified Dielectric Ceramics
DEPARTMENT OF PG STUDIES AND RESEARCH IN MATERIALS SCIENCE, GUG. Page 59
94. Y.B.Xu, T.Liu, Y.Y.He, X.Yuan, “Dielectric properties of Ba0.6Sr0.4TiO3-
Sr(Ga0.5Ta0.5)O3 solid solutions”, IEEE Trans. Ultrason. Ferroelectr. Freq. Control,
55 2369-76 (2008)
95. Y.Li, Y.Qu, “Dielectric properties and substitution mechanism of samarium-
doped Ba0.68 Sr0.32TiO3 ceramics”, Mater. Res. Bull., 44 82-85 (2009)
96. S.B.Reddy, K.P.Rao, M.S.R.Rao, “Dielectric relaxation on Ba1-xBi2x/3Zr0.25Ti0.75O3
Ceramics”, J. Alloys Comp., 481 692-696 (2009)
97. P.Pasierb, M.Osiadly, S.Komornicki, M.Rekas, “Structural and electrical
properties of BaCe(Ti,Y)O3 protonic conductors”, J. Power. Sources, 196 6205-
6209 (2011)
98. P.Kumar, S.Singh, J.K.Juneja, C.Prakash, K.K.Raina, “Influence of calcium
substitution on structural and electrical properties of substituted barium
titanate”, Ceram. Inter., 37 1697-1700 (2011)
* * * * *